【摘 要】
：
研究了不同Ａｌ、Ｔｉ、Ｎｂ含量对ＧＨ９８４合金性能及γ′相析出的影响。结果表明，随Ａｌ、Ｔｉ、Ｎｂ含量增加，合金的室温拉伸强度、７００℃持久寿命和γ′相数量不断增加。Ｎｂ含量为１．３５％时出现持久寿命峰值。在该合金中Ａｌ、
论文部分内容阅读
研究了不同Ａｌ、Ｔｉ、Ｎｂ含量对ＧＨ９８４合金性能及γ′相析出的影响。结果表明，随Ａｌ、Ｔｉ、Ｎｂ含量增加，合金的室温拉伸强度、７００℃持久寿命和γ′相数量不断增加。Ｎｂ含量为１．３５％时出现持久寿命峰值。在该合金中Ａｌ、Ｔｉ、Ｎｂ含量（％）分别控制在０．６５、１．２４和１．３５附近时综合性能最佳。合金管材经舰船海上１０年运行考核，完全可以满足舰船长期使用要求。
The effects of different contents of Al, Ti and Nb on the properties of GH984 alloy and precipitation of γ ’phase were studied. The results show that with the increase of Al, Ti and Nb contents, the tensile strength at room temperature, the long life of 700 ℃ and the number of γ ’phase increase. The peak value of longevity appears when the Nb content is 1.35%. In the alloy Al, Ti, Nb content (%) were controlled at 0.65, 1.24 and 1.35 near the best overall performance. Alloy pipe by the ship 10 years operating assessment at sea, fully meet the long-term requirements of the ship.
其他文献
系统地研究了四异丙氧基酞菁的质子化和脱质子化对吸收和发射光谱的影响．研究表明，三氟乙酸可对酞菁分子连续质子化，分别生成[H2Pc(OiPr)4·H+]+和[H2Pc(OiPr)4·2H+]2+而硫酸可
在ＬｉＮｂＯ３中掺入ＺｎＯ，用提拉法生长Ｚｎ：ＬｉＮｂＯ３晶体。测试了晶体的红外透射光谱、抗光损伤能力、光电导和倍频性能。研究和探讨了高掺锌铌酸锂晶体抗光损伤增强的机理。
新一代S40的出现,为原本以稳重和安全见长的沃尔沃品牌融入了更多新鲜的、年轻化的活力因子。真要告诉年轻才俊们一个好消息,你们在买车时又多了一个新选择——长安沃尔沃S40
一级方程式的赛场在近50年的历史上,世界一级方程式锦标赛先后在24个国家举办过比赛,而从1984年开始,F1运动一个赛季的比赛场次就被限定在16次,不过也有一次例外的情况,那就
[目的]了解和探讨医学研究生个性特征和心理卫生状况。[方法]采用自编一般人口学资料调查表、中国版明尼苏达多项个性测查表(MMPI)对354名医学硕士研究生进行整群抽样、现况
目的构建针对insig-1基因的siRNA表达载体,观察其对炎症状态下RAW264.7小鼠巨噬细胞胆固醇代谢的影响。方法根据insig-1核苷酸序列,设计并构建针对insig-1基因mRNA的3个特异
由铁锰羰基簇混合制备的高分散Ｆｅ－Ｍｎ催化剂，对低碳烯烃来说，比簇衍生的铁催化剂表现出较高的ＣＯ加氢选择性，和较长的寿命。本文用Ｍｎ、Ｆｅ的Ｋ边ＸＡＮＥＳ谱研究了加入到铁体系中的锰组分的作用。结果表明
１前言对埋入地下的钢质管道必须采用阴极保护以延长管道的使用寿命。这一电化学防腐技术已大量应用于石油、化工、煤气、自来水等行业，取得了巨大的经济效益。对于正常铺设的地
11-Oxo-10,11-dihydroxy-5H-indolo[3,2,b]quinoline 7-carboxylic acid was obtained specifically by polyphosphorous acid catalyzed cyclization with optimal reaction
采用丁腈橡胶（ＮＢＲ）及其氢化还原后产物（ＨＮＢＲ）为ＰＶＣ／ＨＤＰＥ共混体系的增容剂，研究了增容剂结构、用量及丙烯腈含量对共混体系相容性的影响。发现丁腈橡胶（ＮＢＲ２９及ＨＮＢＲ２９）对ＰＶＣ／ＨＤＰＥ体系有较好的增容作用，而ＮＢＲ４０及ＨＮＢＲ４０较差。当增容剂