Microstructure and Thermal Physical Parameters of Ni60-Cr3C2 Composite Coating by Laser Cladding
【机 构】
:
Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan Univ
【出 处】
:
武汉理工大学学报(材料科学版)(英文版)
【发表日期】
:
2010年6期
其他文献
Astabilizedsoilstructureformation model wasintroduced. In ordertoformcompact stabilized soil structure, cementitious hydrates were needed to wrap and bind the soil aggregates.Meanwhile, expansible hydrates were needed to squeeze and fill the pores, especi
Degradation of Pore Structure and Microstructures in Hardened Cement Paste Subjected to Flexural Loa
Hardened cement paste was subjected to the flexural loading and wet-dry cycles in sea water.The degradation of microstructures was obtained using scanning electron microscope(SEM),and the energy dispersive spectrum(EDS)analysis was carried to analyze the
A new type of cement was prepared with ground limestone powder,blastfurnace slag,steel slag and gypsum without calcination.The fraction of ground limestone powder in the cement was as high as 40 wt%-60 wt%without Portland clinker.All of its physical prope
Effects of Curing Systems on Properties of High Volume Fine Mineral Powder RPC and Appearance of Hyd
Three kinds of superalloys were prepared by spray deposited process.The analysis results of microstructures and mechanical properties indicate that the spray deposited preforms with higher integral densification and the oxygen content in each kind of supe
To identify the re-arrangement of constituent atoms of an amorphous Mg_(65)Cu_(25)Gd_(10)alloy happened with annealing, structure relaxation of the alloy was investigated as a function of an-nealing time at 373 K through extended X-ray absorption fine str