【摘 要】
：
对某油田发生的φ177.8mm×10.36mm N80Q LC套管滑脱事故进行调研,并对其失效原因进行分析。结果表明,接箍屈服强度,管体屈服强度、抗拉强度不符合标准要求。由于套管管体强
【机 构】
：
中国石油天然气集团石油管工程技术研究院,
论文部分内容阅读
对某油田发生的φ177.8mm×10.36mm N80Q LC套管滑脱事故进行调研,并对其失效原因进行分析。结果表明,接箍屈服强度,管体屈服强度、抗拉强度不符合标准要求。由于套管管体强度偏低而接箍的屈服强度偏高,材料匹配不合适,塑性较低的管体先发生屈服,导致螺纹连接部位易发生粘扣,降低接头连接强度。螺纹参数不合格、抗粘扣性能差是套管螺纹滑脱失效的原因。
The φ177.8mm × 10.36mm N80Q LC casing slip occurred in an oilfield was investigated and the cause of failure was analyzed. The results show that the coupling yield strength, yield strength and tensile strength of the pipe do not meet the standard requirements. Due to the low strength of the casing pipe and the high yield strength of the coupling, the material is not matched properly. The pipe with lower plasticity first yields, which leads to the tripping of the threaded connection part and the decrease of the connection strength. Thread parameters failed, anti-tripping performance is poor thread threading failure reasons.
其他文献
通过金相组织分析,研究了不同均匀化温度和保温时间条件下铸态Mg-Gd-Y-Nd-Zr合金的显微组织,分析了均匀化温度和保温时间对铸态合金组织的影响。结果表明,经530℃保温24h均匀
采用有限元软件模拟了不同板厚下,NM500高强薄钢板辊式淬火过程钢板温度、应力及变形变化规律。结果表明,随着板厚的增加,钢板厚度方向温差增大,冷却速度明显下降。钢板长度
对抽油杆用D级35Mn2钢进行了不同工艺的热处理,并进行了磨损试验、冲击试验和弯曲试验和分析。结果表明:改进抽油杆用钢的热处理工艺,可以有效改善抽油杆抵抗磨损变形、冲击
采用DSC、TEM及XRD检测手段,对在不同冷热结合预处理状态下,Fe65Ni1Al5Ga2P8.65B9.6Si3C5.75非晶条带晶化后的纳米晶形成及晶化体积分数进行了分析研究。结果表明:随预退火温
一革命根據地的建立一九二七年國民黨反動派叛賣了革命,他們與帝國主義者和封建主義者結成了同盟,‘背信棄義地向着中國共產黨與中國人民来一個突然的襲擊,生氣蓬勃的中國大
回顾了铝合金的形变、热处理强化的研究现状,从研究内容、研究对象以及研究方法三个方面总结了形变热处理近10年来研究发生的变化,并综合论述了当下最新的研究成果;进一步展
利用光学显微镜对ST12钢板在拉深及再结晶退火后的不同部位显微组织进行了观察。结果表明:ST12钢拉深后,圆角区域的铁素体晶粒发生了拉伸变形,直壁中间区域的组织演变与圆角
房地产业是我国国民经济重要的支柱产业之一,同时又承担着非常重要的社会保障功能。这种二元属性的存在,使得房地产开发尤其是住宅开发行业的发展深受行业政策影响。现行的城
通过宏微观形貌观察、金相检验、化学成分分析、压缩及硬度测试等方法,对某大型HDPE挤出机推力轴承盘断裂原因进行分析。结果表明:该推力轴承盘与轴承套圈挤压形成的压痕对推
实验选用Al-Mg-Si-Cu铝合金板材为实验材料,对其时效工艺进行了研究。结果表明:第二次时效温度较低时,短时一次时效可获得较高的强度。
The experiment selected Al-Mg-Si-C