The effects of alloying elements, electromagnetic stirring, reheating and semi-solid formation on the microstructure and mechanical properties of Al-Fe alloys prepared by semi-solid formation were studied. It was found that alloying elements and electromagnetic stirring can alter the morphology and growth mode of the iron-rich phase in Al-Fe alloys; and effectively refine the primary Al3Fe phase. In contrast to the microstructure obtained in conventional casting, the Al3Fe phase becomes thin short rod-like instead of thick needle-like; and the dendritic grain structure almost disappears in the semi-solid formation. The Al3Fe phase can be further refined through being dissolved or fused during subsequent reheating. It was also found that the larger extrusion ratio of semi-solid formation causes a greater crushing effect and therefore the Al3Fe phase is more refined and has more uniform distribution. Moreover, Al-Fe alloys prepared by semi-solid formation exhibit excellent mechanical properties at both room and high temperatures. The effects of alloying elements, electromagnetic stirring, reheating and semi-solid formation on the microstructure and mechanical properties of Al-Fe alloys prepared by semi-solid formation were studied. It was found that alloying elements and electromagnetic stirring can alter the morphology and growth. mode of the iron-rich phase in Al-Fe alloys; and effectively refine the primary Al3Fe phase. In contrast to the microstructure obtained in conventional casting, the Al3Fe phase becomes thin short rod-like instead of thick needle- like; and the dendritic grain was almost disappears in the semi-solid formation. It was also found that the larger extrusion ratio of semi-solid formation causes a greater crushing effect and therefore the the Al3Fe phase is more refined and has more uniform distribution. Moreover, Al-Fe alloys prepared by semi-solid formation exhibit excellent mechanical pro perties at both room and high temperatures.