论文部分内容阅读
The preparation and some mechanical,thermal and magnetic properties of the as cast bulk composite Fe72B19.2Si4.8M4 (M=Nb,Mo) alloys obtained by suction casting are presented and discussed.The microstructrural results showed the existence of a crystalline α-Fe(Si) phase embedded in a glassy matrix.The values of microhardness (Hv) and yield strength (σy) for the Nb-containing alloy are exceptionally high,i.e.(12.65±0.3) GPa and (4.22±0.10) GPa,respectively.The saturation polarization values are found to be as high as 1.24 T for both composite alloys.It is thought that the interplay between the secondary crystalline phases and amorphous matrix could be responsible for the mechanical and magnetic behaviour of these alloys.
The preparation and some mechanical, thermal and magnetic properties of the as cast bulk composite Fe72B19.2Si4.8M4 (M = Nb, Mo) alloys obtained by suction casting are presented and discussed. The microstructrural results showed the existence of a crystalline α-Fe (Si) phase embedded in a glassy matrix. The values of microhardness (Hv) and yield strength (σy) for the Nb-containing alloy are exceptionally high, ie (12.65 ± 0.3) GPa and (4.22 ± 0.10) GPa, respectively. It is thought that the interplay between the secondary crystalline phases and the amorphous matrix could be for the mechanical and magnetic behavior of these alloys.