论文部分内容阅读
摘要：现用于建筑行业的原材料及施工技术也都有了很大程度的提高。CL剪力墙是整个建筑的支撑点之一，其质量直接影响着建筑物的整体质量。目前CL剪力墙的施工都是采用自密实混凝土而制成，因此对于自密实混凝土质量的控制才是CL剪力墙的重中之重。文章分别从自密实混凝土的原料、配合比、施工工艺、浇筑和养护几方面来说明其质量控制措施。
关键词：CL剪力墙；自密实混凝土；质量控制
Abstract： is used for raw materials and construction technology ofthe construction industry also has improved to a great extent. CL shear wall is one of the supporting point of the whole building, itsquality directly affects the overall quality of buildings. Theconstruction of CL shear walls are made of self-compacting concrete, so for the control of self-compacting concrete quality is thepriority among priorities of CL shear walls. This paper respectively from raw material, mix self-compacting concrete aspects ratio,construction technology, construction and maintenance to illustrate its quality control measures.
keyword：CL shear wall; self-compacting concrete; quality control
中图分类号：TU71文献标识码：A文章编号：2095-2104(2013)
0.引言
自密实混凝土是一种依靠自身重力来产生流动，保证密实性，就算模板拥有致密钢筋中也能保证填充的密实性、匀质性较好且不需要进行振捣的混凝土。现自密实混凝土已广泛应用于各类建筑的施工当中，成为了建筑行业的“十项新技术”之一。但是因原材料的差异及配合比的不同而使得自密实混凝土的质量很难控制，因而现自密实混凝土的质量控制成为了人们研究的重点。
1.混凝土原材料质量控制
自密实混凝土的原料主要包括水泥、细骨料、粗骨料、外加剂、矿物掺合料以及水等[1]。对于自密实混凝土质量的控制，最为基础的就是对于原材料质量的。在控制原材料质量时应注意以下几点：第一，因自密实混凝土需要加入矿物掺和料，因此选择水泥时就注意选择普通的硅酸盐水泥，因其所含的矿物掺和料较少或没有，可保证混凝土的强度以及其强度增长的速度。第二，要选择细度模数较大的中砂作为细骨料，并且要保证砂的含泥量要保持在1%以内，以保证混凝土的粘聚性，同时还可减少外加剂及水的使用量。第三，粗骨料应选择连续级配的石子，同时要注意所含针片状石子要保持在10%以内，孔隙率要在40%以内，以避免增加水泥浆的用量，同时还能减少水化热及干缩的现象。石子的粒径不能超过25mm，若CL剪力墙需要配筋，那么石子的料径不能超过20mm，以避免出现分层或是离析情况[2]。第四，若只使用水泥来拌合自密实混凝土其成本较高，因此需要加入矿物掺合料。矿物掺合料可选择粉煤灰及矿粉双层加入，以保证自密实混凝土的耐久性及稳定性。第五，外加剂对于自密实混凝土来说非常重要，其直接影响了整个混凝土的性能，一般来说，外加剂可选择使用羧酸系减水剂，因其缓释及空间位阻作用较强，可有效控制自密实混凝土的坍落度，且不影响混凝土的硬化速度，另外其还具强抗缩性，使混凝土的耐久性强。第六，水则可使用普通的自来水。
2.配合比的确定
基于自密实混凝土的特征，其配合比的设计方法自然也与普通混凝土的设计方法不同。但至今为止关于自密实混凝土配合比的设计方法却未统一，通常是利用经验结合试验来共同完成，具有很大的局限性。现使用得比较多的自密实混凝土配合比的设计方法主要有以下几种：固定砂石体积法、改进全计算法和参数法。通过实践发现其中最为科学、合理的方法便是固定砂石体积法，其所使用的参数明确、设计结果清晰，且其理论基础较好，具有强适用性，因此多采用固定砂石体积法来设计自密实混凝土的配合比。
固定砂石体积法最初是由岗村甫提出，其主要是在对自密实混凝土的流动性及抗离析性进行分析的基础上，结合影响配合比的因素，通过试验及研究以确定最终与自密实混凝土特征与需求相符的配合比。因此要分析自密实混凝土的配置强度、水胶比、用水量、砂率、矿物掺合料以及膨胀剂的使用量等，然后再通过性能试验对混合比进行反复调整。自密实混凝土的性能主要有流动性、抗离析性以及填充性。配合比恰当的自密实混凝土应具有以下特点：砂率高、水胶比低、矿物掺合料含量较高。具体自密实混凝土的性能应满足的要求可见表1。
3.混凝土施工工艺控制
自密实混凝土进行搅拌时所采用工艺类似于普通混凝土，但其所使用的搅拌机、搅拌时间、投料顺序和投料精度还是有所不同。因自密实混凝土的粘性较大，故要选择强制式的搅拌机以保证搅拌的均匀性；搅拌时间要比普通混凝土更长，以保证各原材料充分混合；自密实混凝土的投料应先投入胶凝材料进行干拌，搅拌均匀以后加入砂石进行干拌，搅拌均匀以后加入水和外加剂，也可选择将胶凝材料、砂、外加剂和水加入搅拌均匀以后再加入石子进行搅拌。除此之外还要注意投料的精度，一般来说，自密实混凝土投料的精度要保持在±1.4%的水泥、±0.9%的砂、±0.9%的石子、±2%的矿物掺合料、±2%的外加剂以及±1.5%的水，重点以骨料为主。另外在生产时要注意根据骨料的含水率来调节用水量。
4.混凝土浇筑控制
因自密实混凝土的流动性较强，因此要以液压核算来计算模板的侧压力。相比于普通的混凝土，自密实混凝土的屈服值较低，其完全不能支撑自身的重力。因此在浇筑时，位于下层的模板其所受到的侧向压力会根据浇筑高度的不断增加而不断增长，所以浇筑自密实混凝土时其所需要的模板风度及硬度要更强，应选择钢模进行自密实混凝土的浇筑。
在浇筑自密实混凝土之前要对模板的支撑体系进行检查，看其支撑是否到位，模板内是否存在杂物，若有则要进行清理。其次，为避免出现漏浆的情况，要将自密实混凝土的模板缝隙不能超过1.5mm。在浇筑自密实混凝土時还要注意浇筑的高度，一般来说，若是垂直下落，其高度要保持在2m以内；若是水平浇筑，其水平流动距离要保持在10m以内；若配筋比较密集且自密实混凝土本身就具有高粘性，那么可利用在人工敲击等方法在模板外侧进行辅助振捣而加强其密实性，此方法还可将混凝土表面的气泡消除以使混凝土的流动更快。另外，自密实混凝土在进行泵送时要注意保持其连续性。除此之外还要有专门的技术人员在施工现场进行监督，以保证混凝土质量的均匀性及稳定性，若有问题要立即暂停施工进行调整。
5.混凝土的养护
因自密实混凝土的流动性较强，在浇筑以后其可自动找平，但还是会出现突起石子，因此还需要进行人工抹面找平。找平之后就要进行覆膜以避免因水分蒸发而产生收缩裂缝。混凝土终凝之后要进行至少14天的洒水养护，以保持表面的湿润度。
6.结语
自密实混凝土的质量不仅与其本身原材料、配合比有关，同时也与施工工艺、运输、浇筑及后期的养护有关，同时施工人员的技术也会直接影响到其质量。因此要使自密实混凝土的质量得到保障，就需要注意原材料的选择、配合比的确定、运输方式及浇筑工艺，同时还要注意后期的养护以及施工人员的技术水平培训，这样才能尽可能全面地保障自密实混凝土的质量，以保证CL剪力墙的施工质量，保障整个建筑的施工质量。
【参考文献】
[1]廖德祥.自密实混凝土施工质量控制要点[J].中国高新技术企业.2009(04)
[2]刘国铭.自密实混凝土施工技术及其质量控制[J].建设科技.2011(12)
关键词：CL剪力墙；自密实混凝土；质量控制
Abstract： is used for raw materials and construction technology ofthe construction industry also has improved to a great extent. CL shear wall is one of the supporting point of the whole building, itsquality directly affects the overall quality of buildings. Theconstruction of CL shear walls are made of self-compacting concrete, so for the control of self-compacting concrete quality is thepriority among priorities of CL shear walls. This paper respectively from raw material, mix self-compacting concrete aspects ratio,construction technology, construction and maintenance to illustrate its quality control measures.
keyword：CL shear wall; self-compacting concrete; quality control
中图分类号：TU71文献标识码：A文章编号：2095-2104(2013)
0.引言
自密实混凝土是一种依靠自身重力来产生流动，保证密实性，就算模板拥有致密钢筋中也能保证填充的密实性、匀质性较好且不需要进行振捣的混凝土。现自密实混凝土已广泛应用于各类建筑的施工当中，成为了建筑行业的“十项新技术”之一。但是因原材料的差异及配合比的不同而使得自密实混凝土的质量很难控制，因而现自密实混凝土的质量控制成为了人们研究的重点。
1.混凝土原材料质量控制
自密实混凝土的原料主要包括水泥、细骨料、粗骨料、外加剂、矿物掺合料以及水等[1]。对于自密实混凝土质量的控制，最为基础的就是对于原材料质量的。在控制原材料质量时应注意以下几点：第一，因自密实混凝土需要加入矿物掺和料，因此选择水泥时就注意选择普通的硅酸盐水泥，因其所含的矿物掺和料较少或没有，可保证混凝土的强度以及其强度增长的速度。第二，要选择细度模数较大的中砂作为细骨料，并且要保证砂的含泥量要保持在1%以内，以保证混凝土的粘聚性，同时还可减少外加剂及水的使用量。第三，粗骨料应选择连续级配的石子，同时要注意所含针片状石子要保持在10%以内，孔隙率要在40%以内，以避免增加水泥浆的用量，同时还能减少水化热及干缩的现象。石子的粒径不能超过25mm，若CL剪力墙需要配筋，那么石子的料径不能超过20mm，以避免出现分层或是离析情况[2]。第四，若只使用水泥来拌合自密实混凝土其成本较高，因此需要加入矿物掺合料。矿物掺合料可选择粉煤灰及矿粉双层加入，以保证自密实混凝土的耐久性及稳定性。第五，外加剂对于自密实混凝土来说非常重要，其直接影响了整个混凝土的性能，一般来说，外加剂可选择使用羧酸系减水剂，因其缓释及空间位阻作用较强，可有效控制自密实混凝土的坍落度，且不影响混凝土的硬化速度，另外其还具强抗缩性，使混凝土的耐久性强。第六，水则可使用普通的自来水。
2.配合比的确定
基于自密实混凝土的特征，其配合比的设计方法自然也与普通混凝土的设计方法不同。但至今为止关于自密实混凝土配合比的设计方法却未统一，通常是利用经验结合试验来共同完成，具有很大的局限性。现使用得比较多的自密实混凝土配合比的设计方法主要有以下几种：固定砂石体积法、改进全计算法和参数法。通过实践发现其中最为科学、合理的方法便是固定砂石体积法，其所使用的参数明确、设计结果清晰，且其理论基础较好，具有强适用性，因此多采用固定砂石体积法来设计自密实混凝土的配合比。
固定砂石体积法最初是由岗村甫提出，其主要是在对自密实混凝土的流动性及抗离析性进行分析的基础上，结合影响配合比的因素，通过试验及研究以确定最终与自密实混凝土特征与需求相符的配合比。因此要分析自密实混凝土的配置强度、水胶比、用水量、砂率、矿物掺合料以及膨胀剂的使用量等，然后再通过性能试验对混合比进行反复调整。自密实混凝土的性能主要有流动性、抗离析性以及填充性。配合比恰当的自密实混凝土应具有以下特点：砂率高、水胶比低、矿物掺合料含量较高。具体自密实混凝土的性能应满足的要求可见表1。
3.混凝土施工工艺控制
自密实混凝土进行搅拌时所采用工艺类似于普通混凝土，但其所使用的搅拌机、搅拌时间、投料顺序和投料精度还是有所不同。因自密实混凝土的粘性较大，故要选择强制式的搅拌机以保证搅拌的均匀性；搅拌时间要比普通混凝土更长，以保证各原材料充分混合；自密实混凝土的投料应先投入胶凝材料进行干拌，搅拌均匀以后加入砂石进行干拌，搅拌均匀以后加入水和外加剂，也可选择将胶凝材料、砂、外加剂和水加入搅拌均匀以后再加入石子进行搅拌。除此之外还要注意投料的精度，一般来说，自密实混凝土投料的精度要保持在±1.4%的水泥、±0.9%的砂、±0.9%的石子、±2%的矿物掺合料、±2%的外加剂以及±1.5%的水，重点以骨料为主。另外在生产时要注意根据骨料的含水率来调节用水量。
4.混凝土浇筑控制
因自密实混凝土的流动性较强，因此要以液压核算来计算模板的侧压力。相比于普通的混凝土，自密实混凝土的屈服值较低，其完全不能支撑自身的重力。因此在浇筑时，位于下层的模板其所受到的侧向压力会根据浇筑高度的不断增加而不断增长，所以浇筑自密实混凝土时其所需要的模板风度及硬度要更强，应选择钢模进行自密实混凝土的浇筑。
在浇筑自密实混凝土之前要对模板的支撑体系进行检查，看其支撑是否到位，模板内是否存在杂物，若有则要进行清理。其次，为避免出现漏浆的情况，要将自密实混凝土的模板缝隙不能超过1.5mm。在浇筑自密实混凝土時还要注意浇筑的高度，一般来说，若是垂直下落，其高度要保持在2m以内；若是水平浇筑，其水平流动距离要保持在10m以内；若配筋比较密集且自密实混凝土本身就具有高粘性，那么可利用在人工敲击等方法在模板外侧进行辅助振捣而加强其密实性，此方法还可将混凝土表面的气泡消除以使混凝土的流动更快。另外，自密实混凝土在进行泵送时要注意保持其连续性。除此之外还要有专门的技术人员在施工现场进行监督，以保证混凝土质量的均匀性及稳定性，若有问题要立即暂停施工进行调整。
5.混凝土的养护
因自密实混凝土的流动性较强，在浇筑以后其可自动找平，但还是会出现突起石子，因此还需要进行人工抹面找平。找平之后就要进行覆膜以避免因水分蒸发而产生收缩裂缝。混凝土终凝之后要进行至少14天的洒水养护，以保持表面的湿润度。
6.结语
自密实混凝土的质量不仅与其本身原材料、配合比有关，同时也与施工工艺、运输、浇筑及后期的养护有关，同时施工人员的技术也会直接影响到其质量。因此要使自密实混凝土的质量得到保障，就需要注意原材料的选择、配合比的确定、运输方式及浇筑工艺，同时还要注意后期的养护以及施工人员的技术水平培训，这样才能尽可能全面地保障自密实混凝土的质量，以保证CL剪力墙的施工质量，保障整个建筑的施工质量。
【参考文献】
[1]廖德祥.自密实混凝土施工质量控制要点[J].中国高新技术企业.2009(04)
[2]刘国铭.自密实混凝土施工技术及其质量控制[J].建设科技.2011(12)