The behavior of Si1-xGex/Si heterostructures under different annealing conditions has been studied. It is found that while RTA treatment diminishes the point defects, it introduces the misfit dislocations into Si1-xGex layers at same time. Higher annealing temperature will result in the propagation of misfit dislocations and then the total destruction of the crystal quality.