【摘 要】
：
对银包覆Ｂｉ２２２３高温超导带材的热压作了系统试验研究，确定了合理的带材热压处理工艺规范。结果表明热压处理能提高超导带中粉芯的密度和晶粒织构度，从而提高超导带材临界电流密度Ｊｃ。超
论文部分内容阅读
对银包覆Ｂｉ２２２３高温超导带材的热压作了系统试验研究，确定了合理的带材热压处理工艺规范。结果表明热压处理能提高超导带中粉芯的密度和晶粒织构度，从而提高超导带材临界电流密度Ｊｃ。超导带材的Ｊｃ与热压的温度、压力、热压与冷压的结合方式等有密切的关系。最大的Ｊｃ为２．２×１０４Ａ／ｃｍ２，７７Ｋ，０Ｔ。
The hot pressing of silver-coated Bi2223 high-temperature superconducting tapes was systematically studied, and the reasonable specification of hot-pressing process of tapes was confirmed. The results show that hot pressing can increase the density and grain structure of the cored wire in the superconducting tape and thus increase the critical current density Jc of the superconducting tape. Jc superconducting tape and hot pressing temperature, pressure, hot and cold combination of pressure and other methods are closely related. The maximum Jc is 2.2 × 104A / cm2, 77K, 0T.
其他文献
财政在国有企业重组与提高竞争力过程中需要理清四个问题: 1.确定财政干预国有企业重组的有效范围,强化财政基础。在国有经济占主导地位的经济体制下,要求财政以国有资产所
FDA今天宣布了一项新倡议,以解决外部输液泵的安全问题。外部输液泵在一定的控制程序下,将营养或药物等液体递送至患者体内。
FDA today announced a new initiative to ad
本文通过压力容器内外壁周长差导出两个经验公式，借此可对透照部位快速对中。
In this paper, we derive two empirical formulas based on the difference in the circumfer
用TPD和脉冲微型反应器分别测定了HZSM-5上CO_2和NH_3的吸附量及乙醇脱水反应的活性和选择性。HZSM-5吸附NH_3后的TPD谱图上出现两个峰,T_M值分别为 296和500℃。随着Na交换
加强专项资金监管,确保专项资金安全有效运行,是监察机关深入落实“三个代表”重要思想的具体体现,也是党风廉政建设和反腐败斗争的重要内容。近年来,监察部及三峡建委监察局
全球市场调查有着自己的法则。想用一套“标准法则”来对全球不同地域、不同文化背景的市场进行调查,那么必定会失败,会遇到“翻船”的厄运。只有按照它自身的规律一步一步进
以SiO_2、NaAlO_2、NaOH、KOH、TPAOH、NH_4HCO_3·NH_2COONH_4和H_2O(51∶1∶9∶0.5∶12∶9∶1300mol比)为原料,在压热釜中170℃晶化10天;洗涤、干燥;通N_2 450℃活化8 h,65
变电站10kV线路容易发生越级跳闸问题,从而导致设备发生故障,对变电站设备的安全以及电网运行安全造成巨大威胁.本文简单概述变电站10kV线路越级跳闸现象,分析越级跳闸问题的
社会飞速发展的今天,随着经济、文化的进步,人们对居住环境的要求越来越高。特别是对个性化、舒适、温馨的家庭环境需求日益剧增,这促进了室内设计的发展。“轻装修,重装饰”