摘要：建筑工程中混凝土产生的裂缝有很多,对工程质量具有不同程度的危害。楼面结构出现裂缝原因非常复杂，有混凝土原材料拌合、温度变化及施工等方面问题。混凝土楼面裂缝的存在和发展，会降低结构的承载力和耐久性。本文从多方面分析了现浇混凝土楼面裂缝产生的原因，并提出了预防混凝土楼面裂缝的措施及处理方法，以确保混凝土楼面质量，减少裂缝的发生。
关键词：现浇混凝土，楼面裂缝，防治措施，处理方法
Abstract: the concrete in the construction engineering produced many cracks, and the engineering quality with a different degree of harm. Floor structure crack reasons for this are complex, white of the raw materials, change of temperature and construction problems. Cracks in the concrete floor existence and development, will reduce the bearing capacity of the structure and durability. This paper analyzed from various cast-in-situ concrete floor cracks reasons and puts forward the prevention of cracks in the concrete floor measures and solutions, to ensure the concrete floor quality, reduce the occurrence of cracks.
Keywords: cast-in-situ concrete, floor cracks, prevention and control measures, the treatment method
中图分类号：TU37文献标识码：A 文章编号：
现浇混凝土楼面裂缝的成因复杂，甚至多种因素相互影响，如不能很好的控制和处理，会降低结构的承载力和耐久性。
一、现浇混凝土楼面裂缝成因分析
1、混凝土因收缩及温度变化引起楼面裂缝
混凝土澆筑完成后，水泥的水化或混凝土中水分的蒸发会引起混凝土干缩，从而产生裂缝。混凝土表面若不能及时覆盖，特别是楼板在炎热天气浇筑混凝土后，楼板表层混凝土水分蒸发的速度比内部快得多,表层混凝土的收缩较大，内部相对收缩较小，导致混凝土产生拉应力,因此混凝土表层很容易产生塑性开裂。混凝土中水分蒸发速度越快，混凝土收缩裂缝越容易发生。混凝土硬化期间水泥放出大量水化热,内部温度不断上升,在表面引起拉应力。后期在降温过程中,气温的降低也会在混凝土表面引起很大的拉应力。当这些拉应力超出混凝土的抗裂能力时,即会出现裂缝。
2、混凝土自身质量引起楼面裂缝
商品混凝土为了达到泵送要求，需要混凝土有很好的流动性，混凝土塌落度也较大，其水分容易散失，表面容易形成裂缝。水泥强度等级越高、早期强度越高，对混凝土开裂影响越大。水灰比选择不当，造成混凝土的和易性差，导致混凝土离析，增加收缩值。
3、混凝土楼面因外部荷载引起的裂缝现有很多工程因建设单位压缩工期，提前实现收益，导致施工单位为了抢工期，在下一层混凝土楼板浇筑后，混凝土刚刚硬化，还没有达到承受荷载的强度时，便开始上一层的施工，施工过程中，还存在人为的对结构损害。在楼板未达到强度的情况下，进行材料、构件堆放，有的甚至大型钢梁、钢柱、大量模板堆积楼面，致使楼板表面和内部结构受到损害，就会出现裂缝。 4、施工和养护不当引起楼面裂缝
（1）现场混凝土浇筑振捣时操作不当，浇捣、振实工序中的任何缺陷和疏漏，都可能是裂缝产生的直接或间接原因。
（2）混凝土楼面在终凝前，没有进行二次抹压，造成混凝土楼面的收缩裂缝。
（3）混凝土降温、保温工作不到位，引起混凝土的内外温差过大，会使混凝土楼面产生温度裂缝。
（4）混凝土楼面养护不到位，造成混凝土早期脱水，混凝土楼面会产生收缩裂缝。混凝土养护，特别是早期养护质量与裂缝的关系密切，混凝土尚处于未完全硬化状态时，如干燥过快，则产生收缩裂缝，通常发生在表面上，裂缝不规则，宽度小。另外水泥在水化及硬化过程中，散发大量热量，使混凝土内外部产生温差，超过一定值时，因混凝土的收缩不一致而产生裂缝。
（5）模板本身质量不好或安装质量存在问题。如模板有孔洞未进行封堵，模板缝隙较大，造成模板漏浆，可能造成混凝土开裂。
（6）拆模过早也可能损坏混凝土楼板边缘或表面，产生裂缝。
（7）钢筋表面锈蚀较重，或有泥土及其它污染、造成钢筋与混凝土之间的握裹力大大降低，钢筋与混凝土会呈分离状态，诱使混凝土内部结构变化产生裂缝。
（8）施工过程中，对楼板钢筋进行了踩踏，未复位；钢筋保护层厚度过小或过大；以及浇筑中碰撞钢筋使其移位等都可能引起裂缝。
二、楼面裂缝防治措施
控制混凝土裂缝，必须从混凝土产生裂缝的几个主要原因入手，才能有效地将裂缝控制在充许范围内。裂缝控制应通过降低混凝土收缩所产生的拉应力，有效地控制混凝土内外温差，合理地配置混凝土，避免过早对混凝土楼面加荷、过早拆模，及加强施工质量控制等方面措施，以减少楼面裂缝的产生。
1、合理地配置混凝土
现施工普遍采用泵送混凝土，因此合理设计配合比是有效控制和预防混凝土裂缝发生的前提。应根据工程所处条件，对砂率、水灰比、水泥用量及掺合料用量等进行优化设计，选择最优方案。
（1）骨料的选择。由于粗骨料对收缩的约束作用，收缩量较小，可减少开裂的可能。粗骨料宜用表面粗糙、质地坚硬的石料、级配良好、空隙率小、无碱性反应，有害物质及粘土含量不超过规定；细骨料宜用颗粒较粗，含泥量较低的中砂。
（2）水泥应选用水化热较低的水泥，严禁使用安定性不合格的水泥。选用中低水化热水泥，可使水泥在拌和过程中水化热释放较小，显著减少混凝土升温。
（3））配制砼时计量应准确，要严格控制水灰比和水泥用量，搅拌均匀，离析的砼必须重新拌匀后，方可浇筑。 采用降低水泥用量的方法来降低混凝土的温升值。
（4）外加剂的选择。混凝土中掺入减水剂，可使混凝土工作性能明显的改善，同时又减少拌和用水，节约水泥，从而降低了水化热。
2、 外部荷载方面的控制措施
（1）施工单位要合理地控制施工进度。每个工序之间要有充足的间歇时间。
（2）在楼板混凝土强度未达到1.2MPa 时不准上人施工。
（3）楼板不能过早堆放荷载。堆载不允许集中，应尽可能均匀放置，以减少楼面集中荷载。
（4）模板和支架要有足够的刚度和稳定性。防止模板支撑不稳或增加荷载后模板下沉较大。对于大开间的楼面应在模板支撑架搭设前就预先采用加密立杆以增加刚度，减少变形来加强该区域的抗冲击振动荷载，并在已浇筑的楼面上铺设木模板以扩散压力，进一步防止裂缝的发生。
3、施工方面的控制措施
（1）加强混凝土的浇灌振捣，提高密实度。浇筑时应防止离析现象，振捣应均匀、适度，根据不同的混凝土坍落度正确掌握振捣时间，避免过振或漏振，宜采用两次振捣技术，改善混凝土强度，提高抗裂性。
（2）对楼板采用二次抹面技术，使楼板混凝土表面更密实。
（3）混凝土不宜过早拆模。合理掌握拆模时机，拆模应保证混凝土不损坏或不开裂。由于施工进度加快。而施工单位又不愿意过多的在模板上投入，这就造成模板周转不足、顶板支撑过早拆模。施工中要严格执行拆模申请制度，只有在同条件养护试块合格的情况下才允许拆模。
（4）加强混凝土的养护。在混凝土裂縫的防治工作中，对混凝土的早期养护工作尤为重要，以保证混凝土在早期尽可能少产生收缩。混凝土浇筑完毕后，应及时进行保温养护，保温养护是混凝土施工的关键环节。在保温养护过程中，应始终保持混凝土表面处于湿润状态。在气温高、湿度低或风速大的条件下，更应及早进行养护。
（5）加强混凝土的降温和保温工作。,施工时应采取必要的降温措施，浇捣成型后，应采取必要的蓄水保温措施，表面覆盖薄膜、湿麻袋等进行养护，以防止由于混凝土内外温差过大而引起的温度裂缝。
（6）避免在雨天或大风中浇灌混凝土。
（7）夏季应注意混凝土的浇捣温度，采用低温人模、低温养护，以降低混凝土原材料的温度。
（8）模板构造要合理，以防止模板各杆件间的变形不同而导致砼裂缝；模板和支架要有足够的刚度，防止施工荷载作用下，模板变形过大造成开裂；模板周转次数不能过多，有损坏的，变形严重的不要使用；模板安装接缝要小，有些接缝不严，需要用胶带进行封堵；孔眼也必须封堵，保证模板不能漏浆。
（9）钢筋表面锈蚀要进行处理；楼板钢筋要合理布置马凳筋，不可随意减少；尽量不要踩踏板的钢筋；混凝土施工过程中的踩踏或钢筋移位，要立即复位；严格控制保护层厚度。
三、楼板裂缝的处理方法
如果楼面已经由于各种原因而产生了裂缝，那么就需要做好妥善处理工作，对不同宽度的裂缝采用适合的方法。
1、对裂缝宽度小于0.3mm的，可用水泥浆体加以封闭即可。灌浆前应清除裂缝内浮灰积水，干燥后再进行灌浆作业。
2、对裂缝宽度小于1.0mm的，可用圆盘锯沿裂缝切出V型槽，宽度8～10mm，深度5mm，用压缩空气吹净浮灰后，采用低粘度环氧树脂类粘结剂对裂缝进行灌浆处理；裂缝宽度大于1.0mm者可直接灌入，灌满为止。
四、结束语
以上是对混凝土裂缝的成因及控制进行了理论和实践上的探讨，同时在实践中的应用效果也是比较好的。混凝土楼板裂缝应以预防为主的原则，要通过合理设计混凝土配合比、正确选用原材料、加强施工控制、严格遵守施工技术规程、提高施工技术水平，这样才有可能最大程度减少混凝土裂缝的产生，尽量减少裂缝造成的危害。
参考文献
[1]GB0010-2002,混凝土结构设计规范[S]
[2] 王海军.大体积混凝土温度和收缩裂缝控制措施.[J].山西建筑.2006.15.
[3] 宋翔.现浇混凝土楼板裂缝及检测《工业建筑》2005年第S1期
[4]吴伯浩.混凝土楼板裂缝实例分析《大众科技》2006年02期
作者简介：
谷波，1972年2月生，山东烟台人，山东泰和建设管理有限公司，项目总监，工程师。
贾黎幸，山东烟台人，山东泰和建设管理有限公司，项目总监，工程师。
关键词：现浇混凝土，楼面裂缝，防治措施，处理方法
Abstract: the concrete in the construction engineering produced many cracks, and the engineering quality with a different degree of harm. Floor structure crack reasons for this are complex, white of the raw materials, change of temperature and construction problems. Cracks in the concrete floor existence and development, will reduce the bearing capacity of the structure and durability. This paper analyzed from various cast-in-situ concrete floor cracks reasons and puts forward the prevention of cracks in the concrete floor measures and solutions, to ensure the concrete floor quality, reduce the occurrence of cracks.
Keywords: cast-in-situ concrete, floor cracks, prevention and control measures, the treatment method
中图分类号：TU37文献标识码：A 文章编号：
现浇混凝土楼面裂缝的成因复杂，甚至多种因素相互影响，如不能很好的控制和处理，会降低结构的承载力和耐久性。
一、现浇混凝土楼面裂缝成因分析
1、混凝土因收缩及温度变化引起楼面裂缝
混凝土澆筑完成后，水泥的水化或混凝土中水分的蒸发会引起混凝土干缩，从而产生裂缝。混凝土表面若不能及时覆盖，特别是楼板在炎热天气浇筑混凝土后，楼板表层混凝土水分蒸发的速度比内部快得多,表层混凝土的收缩较大，内部相对收缩较小，导致混凝土产生拉应力,因此混凝土表层很容易产生塑性开裂。混凝土中水分蒸发速度越快，混凝土收缩裂缝越容易发生。混凝土硬化期间水泥放出大量水化热,内部温度不断上升,在表面引起拉应力。后期在降温过程中,气温的降低也会在混凝土表面引起很大的拉应力。当这些拉应力超出混凝土的抗裂能力时,即会出现裂缝。
2、混凝土自身质量引起楼面裂缝
商品混凝土为了达到泵送要求，需要混凝土有很好的流动性，混凝土塌落度也较大，其水分容易散失，表面容易形成裂缝。水泥强度等级越高、早期强度越高，对混凝土开裂影响越大。水灰比选择不当，造成混凝土的和易性差，导致混凝土离析，增加收缩值。
3、混凝土楼面因外部荷载引起的裂缝现有很多工程因建设单位压缩工期，提前实现收益，导致施工单位为了抢工期，在下一层混凝土楼板浇筑后，混凝土刚刚硬化，还没有达到承受荷载的强度时，便开始上一层的施工，施工过程中，还存在人为的对结构损害。在楼板未达到强度的情况下，进行材料、构件堆放，有的甚至大型钢梁、钢柱、大量模板堆积楼面，致使楼板表面和内部结构受到损害，就会出现裂缝。 4、施工和养护不当引起楼面裂缝
（1）现场混凝土浇筑振捣时操作不当，浇捣、振实工序中的任何缺陷和疏漏，都可能是裂缝产生的直接或间接原因。
（2）混凝土楼面在终凝前，没有进行二次抹压，造成混凝土楼面的收缩裂缝。
（3）混凝土降温、保温工作不到位，引起混凝土的内外温差过大，会使混凝土楼面产生温度裂缝。
（4）混凝土楼面养护不到位，造成混凝土早期脱水，混凝土楼面会产生收缩裂缝。混凝土养护，特别是早期养护质量与裂缝的关系密切，混凝土尚处于未完全硬化状态时，如干燥过快，则产生收缩裂缝，通常发生在表面上，裂缝不规则，宽度小。另外水泥在水化及硬化过程中，散发大量热量，使混凝土内外部产生温差，超过一定值时，因混凝土的收缩不一致而产生裂缝。
（5）模板本身质量不好或安装质量存在问题。如模板有孔洞未进行封堵，模板缝隙较大，造成模板漏浆，可能造成混凝土开裂。
（6）拆模过早也可能损坏混凝土楼板边缘或表面，产生裂缝。
（7）钢筋表面锈蚀较重，或有泥土及其它污染、造成钢筋与混凝土之间的握裹力大大降低，钢筋与混凝土会呈分离状态，诱使混凝土内部结构变化产生裂缝。
（8）施工过程中，对楼板钢筋进行了踩踏，未复位；钢筋保护层厚度过小或过大；以及浇筑中碰撞钢筋使其移位等都可能引起裂缝。
二、楼面裂缝防治措施
控制混凝土裂缝，必须从混凝土产生裂缝的几个主要原因入手，才能有效地将裂缝控制在充许范围内。裂缝控制应通过降低混凝土收缩所产生的拉应力，有效地控制混凝土内外温差，合理地配置混凝土，避免过早对混凝土楼面加荷、过早拆模，及加强施工质量控制等方面措施，以减少楼面裂缝的产生。
1、合理地配置混凝土
现施工普遍采用泵送混凝土，因此合理设计配合比是有效控制和预防混凝土裂缝发生的前提。应根据工程所处条件，对砂率、水灰比、水泥用量及掺合料用量等进行优化设计，选择最优方案。
（1）骨料的选择。由于粗骨料对收缩的约束作用，收缩量较小，可减少开裂的可能。粗骨料宜用表面粗糙、质地坚硬的石料、级配良好、空隙率小、无碱性反应，有害物质及粘土含量不超过规定；细骨料宜用颗粒较粗，含泥量较低的中砂。
（2）水泥应选用水化热较低的水泥，严禁使用安定性不合格的水泥。选用中低水化热水泥，可使水泥在拌和过程中水化热释放较小，显著减少混凝土升温。
（3））配制砼时计量应准确，要严格控制水灰比和水泥用量，搅拌均匀，离析的砼必须重新拌匀后，方可浇筑。 采用降低水泥用量的方法来降低混凝土的温升值。
（4）外加剂的选择。混凝土中掺入减水剂，可使混凝土工作性能明显的改善，同时又减少拌和用水，节约水泥，从而降低了水化热。
2、 外部荷载方面的控制措施
（1）施工单位要合理地控制施工进度。每个工序之间要有充足的间歇时间。
（2）在楼板混凝土强度未达到1.2MPa 时不准上人施工。
（3）楼板不能过早堆放荷载。堆载不允许集中，应尽可能均匀放置，以减少楼面集中荷载。
（4）模板和支架要有足够的刚度和稳定性。防止模板支撑不稳或增加荷载后模板下沉较大。对于大开间的楼面应在模板支撑架搭设前就预先采用加密立杆以增加刚度，减少变形来加强该区域的抗冲击振动荷载，并在已浇筑的楼面上铺设木模板以扩散压力，进一步防止裂缝的发生。
3、施工方面的控制措施
（1）加强混凝土的浇灌振捣，提高密实度。浇筑时应防止离析现象，振捣应均匀、适度，根据不同的混凝土坍落度正确掌握振捣时间，避免过振或漏振，宜采用两次振捣技术，改善混凝土强度，提高抗裂性。
（2）对楼板采用二次抹面技术，使楼板混凝土表面更密实。
（3）混凝土不宜过早拆模。合理掌握拆模时机，拆模应保证混凝土不损坏或不开裂。由于施工进度加快。而施工单位又不愿意过多的在模板上投入，这就造成模板周转不足、顶板支撑过早拆模。施工中要严格执行拆模申请制度，只有在同条件养护试块合格的情况下才允许拆模。
（4）加强混凝土的养护。在混凝土裂縫的防治工作中，对混凝土的早期养护工作尤为重要，以保证混凝土在早期尽可能少产生收缩。混凝土浇筑完毕后，应及时进行保温养护，保温养护是混凝土施工的关键环节。在保温养护过程中，应始终保持混凝土表面处于湿润状态。在气温高、湿度低或风速大的条件下，更应及早进行养护。
（5）加强混凝土的降温和保温工作。,施工时应采取必要的降温措施，浇捣成型后，应采取必要的蓄水保温措施，表面覆盖薄膜、湿麻袋等进行养护，以防止由于混凝土内外温差过大而引起的温度裂缝。
（6）避免在雨天或大风中浇灌混凝土。
（7）夏季应注意混凝土的浇捣温度，采用低温人模、低温养护，以降低混凝土原材料的温度。
（8）模板构造要合理，以防止模板各杆件间的变形不同而导致砼裂缝；模板和支架要有足够的刚度，防止施工荷载作用下，模板变形过大造成开裂；模板周转次数不能过多，有损坏的，变形严重的不要使用；模板安装接缝要小，有些接缝不严，需要用胶带进行封堵；孔眼也必须封堵，保证模板不能漏浆。
（9）钢筋表面锈蚀要进行处理；楼板钢筋要合理布置马凳筋，不可随意减少；尽量不要踩踏板的钢筋；混凝土施工过程中的踩踏或钢筋移位，要立即复位；严格控制保护层厚度。
三、楼板裂缝的处理方法
如果楼面已经由于各种原因而产生了裂缝，那么就需要做好妥善处理工作，对不同宽度的裂缝采用适合的方法。
1、对裂缝宽度小于0.3mm的，可用水泥浆体加以封闭即可。灌浆前应清除裂缝内浮灰积水，干燥后再进行灌浆作业。
2、对裂缝宽度小于1.0mm的，可用圆盘锯沿裂缝切出V型槽，宽度8～10mm，深度5mm，用压缩空气吹净浮灰后，采用低粘度环氧树脂类粘结剂对裂缝进行灌浆处理；裂缝宽度大于1.0mm者可直接灌入，灌满为止。
四、结束语
以上是对混凝土裂缝的成因及控制进行了理论和实践上的探讨，同时在实践中的应用效果也是比较好的。混凝土楼板裂缝应以预防为主的原则，要通过合理设计混凝土配合比、正确选用原材料、加强施工控制、严格遵守施工技术规程、提高施工技术水平，这样才有可能最大程度减少混凝土裂缝的产生，尽量减少裂缝造成的危害。
参考文献
[1]GB0010-2002,混凝土结构设计规范[S]
[2] 王海军.大体积混凝土温度和收缩裂缝控制措施.[J].山西建筑.2006.15.
[3] 宋翔.现浇混凝土楼板裂缝及检测《工业建筑》2005年第S1期
[4]吴伯浩.混凝土楼板裂缝实例分析《大众科技》2006年02期
作者简介：
谷波，1972年2月生，山东烟台人，山东泰和建设管理有限公司，项目总监，工程师。
贾黎幸，山东烟台人，山东泰和建设管理有限公司，项目总监，工程师。