【摘 要】
:
With alumina sol as binder and Ni metal as sintering aids,the Ni-TiB2/Al2O3 composite cathode material for aluminum electrolysis was prepared by cold-pressed si
【机 构】
:
Rare Metals and Metallurgy Materials Research Institute,General Research Institute for Nonferrous Me
论文部分内容阅读
With alumina sol as binder and Ni metal as sintering aids,the Ni-TiB2/Al2O3 composite cathode material for aluminum electrolysis was prepared by cold-pressed sintering.The mechanical properties of the com-posite cathode material were measured.Its electrolytic properties were identified by a 20-A electrolysis test.Cathode samples before and after electrolysis test were measured by energy-dispersive spectroscopy(EDS).The migration behavior of various elements in the electrolysis process was studied by phase analysis.The result shows that Ni metal can effectively fill the gap between the aggregate during the sintering process,which can improve the sintering density of the composite cathode material significantly.The voltage of the 20-A electrolysis test is stable.The impurity of aluminum liquid is 0.42%.The aluminum liquid can wet the cathode surface effectively,and the Ni-TiB2/Al2O3 composite is an ideal wet-table cathode material.In the process of electrolysis,the alkali elements in the electrolyte penetrate the electrode,where K goes deeper than Na.Al generated on the cathode surface will also penetrate the cathode through the gap of the composite material,while Ni in the electrode will spread into the aluminum liquid layer.
其他文献
The uniaxial tensile tests were carried out at temperature ranging from room temperature(RT)to 523 K under strain rates of 0.001,0.010 and 0.100 s-1 to obtain t
LiVPO4F has attracted increasing research interest in the field of Li-ion batteries due to its high working voltage platform and high theoretical energy density
In order to prove that the Te-based glass frit could be applied to Ag pastes to fabricate Ag electrode and elucidate the reactions among Ag,the frit,and the Si
CeO2 is one of the main catalysts for solid oxide fuel cell(SOFC).It is critical to find a green and cost-effective fabrication method for CeO2 at scale.In this
Battery technologies have obtained great attention due to their wide-ranging applications in present and emerging fields[1,2],and great progress in exploring no
Yb3+and Er3+were doped into Y2O3 to form Y2O3∶Yb3+,Er3+microcrystals.The effect of doping concentration of Yb3+was studied.The near-ultraviolet(UV)upconversion
Aluminum phosphate(AlPO4)was used to modify the surface of LiNi1/3Co1/3Mn1/3O2(NCM)cathode material.The surface structure and electrochemical prop-erties of the
The p-type TiCoSb-based half-Heuslers are widely studied due to the good electrical transport prop-erties after hole doping,while the pristine TiCoSb is intrins
SnO2 is considered to be a promising candidate as anode material for lithium ion batteries,due to its high theoretical specific capacity(1494 mAh·g-1).Neverthe
It is a big challenge to prepare non-rare metal and high-activity electrocatalysts for oxygen reduction reaction(ORR).In this paper,a cobalt/carbon nan-otubes/c