【摘 要】
：
按照Fe-Cr-C合金系堆焊层化学成分及力学性能要求,通过计算确定了几组备选实验方案,通过实验确定最终配方,研制出适用于耐磨硬面堆焊的自保护药芯焊丝。实验证明,所研制的药
【机 构】
：
西安建筑科技大学机电学院耐磨材料研究所,中国舰船研究院,
论文部分内容阅读
按照Fe-Cr-C合金系堆焊层化学成分及力学性能要求,通过计算确定了几组备选实验方案,通过实验确定最终配方,研制出适用于耐磨硬面堆焊的自保护药芯焊丝。实验证明,所研制的药芯焊丝焊接工艺性能良好、焊道成型美观。堆焊层表面裂纹细密,呈网状分布。堆焊层微观组织主要是垂直于基材方向生长的(Cr,Fe)7C3初生碳化物和共晶组织。堆焊层洛氏硬度为62HRC,耐磨性大约为新铸产品的1.5倍。
According to the chemical composition and mechanical properties of Fe-Cr-C alloy surfacing layer, several groups of alternative experimental schemes were determined by calculation. The final formulation was determined through experiments and a self-shielded flux core Wire. Experiments show that the developed flux cored wire welding process performance is good, weld forming beautiful. Surfacing surfacing crack, was reticular distribution. The surfacing layer microstructure is mainly (Cr, Fe) 7C3 primary carbides and eutectic structure grown perpendicular to the substrate. Surfacing Rockwell hardness of 62HRC, wear resistance of about 1.5 times the new cast product.
其他文献
采用Ag-Cu-Ti钎料进行Ti6Al4V(TC4)钛合金和1Cr18Ni9Ti不锈钢的真空钎焊,观察分析了其在钎焊温度为790～870℃和保温时间为1和3min时钎缝界面微观组织和成分分布。研究结果表明
介绍了流程工业中CIMS发展的历史、现状,以及流程工业与离散加工工业的异同。讨论了流程工业中MES(ManufacturingExecutionSystem)作用、功能,给出了当前CIM用于流程工业的一
患者 男 ,74岁。因右眼剧痛 ,伴头痛 ,恶心 ,呕吐 8ｈ ,右眼流血不止 1ｈ ,于 1 998年 7月 2 6日入院。患者有高血压史 1 0多年 ,右眼有青光眼病史 2年 ,已失明。发病前无外伤史
分析了传统埋弧焊控制系统的弊端,并设计了一种新型的埋弧焊控制系统的人机界面。控制核心采用了三星公司的ARM9处理器S3C2440A,使用640*480的TFT液晶显示器。在硬件的基础上
高炉炉顶布料溜槽长期受到硬度较高、速度较大的冶炼料流的冲刷,磨损严重,属于耗损件。为提高溜槽衬板的使用寿命,采用WC作为耐磨层的基体,用锰白铜作为钎料,通过浸润焊接方
表面组装焊点的几何形态是影响焊点可靠性的重要因素之一。本文采用有限元方法,重点讨论了润湿角对低银Sn2.5Ag0.7CuRE焊点的应力应变分布和热疲劳寿命的影响,并与Sn37Pb和Sn
目的 :观察虫草制剂金水宝对维持性血液透析 (MHD)患者外周血T细胞凋亡和FasL表达的影响。方法 :应用流式细胞仪 (FCM)定量检测了 30名MHD患者 (血透组 )、30名MHD加金水宝治
出租用车市场已越来越成为我国轿车厂商激烈争夺的目标市场。这是由出租用车市场的特殊性决定的。出租车用于经营,有别于政府机关的公务车、企业的商务车、私人的私家车。其
通过高周疲劳试验,测定了大厚壁NiCrMoV钢深窄间隙埋弧焊焊接接头的S-N特征曲线。疲劳试验发现,疲劳试样断裂位置多发生在焊缝处,并对疲劳断口进行了SEM分析。发现疲劳裂纹源
面神经瘤是一类发病率较低、较少见的肿瘤。多为良性，生长缓慢，原发于面神经的恶性肿瘤极为罕见。通常依病理特征不同分为：面神经鞘膜瘤、面神经纤维瘤、面神经血管瘤、面神经脑