The addition of 3%～9% Zr on the martensitic transformation of Ti-18Nb(at.%) alloy was investigated. The results of microstructure and X-ray diffraction (XRD) analysis show that the phase constitution of as-quenched Ti-18Nb-9Zr(at.%) alloy consists of the retained matrix and martensite, while that of the other three alloys is single martensite. No trace of athermal phase was found in any of the as-quenched alloys. Unlike the effect of Nb addition on the martensitic transformation start temperature Ms of Ti-18Nb(at.%) alloy, Ms de-creased nonlinearly as increasing the Zr addition from 3% to 9% and Ms decreased much more sharply as increasing the Zr addition. The Ms of as-quenched Ti-18Nb-9Zr alloy was around room temperature. The effect of Zr addition on the phase stabilizing in the Ti-18Nb(at.%) alloy was briefly discussed.
The results of microstructure and X-ray diffraction (XRD) analysis show that the phase constitution of as-quenched Ti- 18Nb-9Zr (at.%) Alloy consists of the retained matrix and martensite, while that of the other three alloys is single martensite. No trace of athermal phase was found in any of the as-quenched alloys. Unlike the effect of Nb addition on the martensitic transformation start temperature Ms of Ti-18Nb (at.%) alloy, Ms de-creased nonlinearly as increasing the Zr addition from 3% to 9% and Ms minus much more sharply as increasing the Zr addition. The Ms of as The effect of Zr addition on the phase stabilizing in the Ti-18Nb (at.%) alloy was briefly discussed.