分析了马氏体相变表象晶体学W-L-R理论不适用于{225}_f马氏体转变的原因,并作了修正,结果表明,修正后的W-L-R理论较成功地预测了不同合金的{225}_f马氏体转变,惯习面的理论预测值均与实验值符合较好,误差小于3.2°。
The reason that WLR theory of martensitic transformation apparent crystallography is not suitable for {225} _f martensite transformation was analyzed and corrected. The results show that the modified WLR theory has successfully predicted {225} _f martensite transformation of different alloys, _f martensitic transformation, the theoretical prediction of habitual surface are in good agreement with the experimental values, the error is less than 3.2 °.