A new citrate acid-hydrazine sol-gel route for preparation of Co3O4 nanoparticles has been developed. Co3O4 nanoparticles with different particle-sizes and morphology were prepared at different heat-treatment temperatures and the pure cubic nanocrystals of Co3O4 were obtained at 600℃. The synthesis process was monitored by infrared spectroscopy (IR), thermal gravimetric and differential thermal analysis (TG-DTA). The structure and morphology of Co3O4 nanocrystals were characterized by X-ray powder diffraction (XRD), transmission electron microscopy (TEM) and X-ray-photoelectron spectroscopy (XPS). The infrared absorption bands blue-shifted with particle size decreasing, which could be attributed to increasing surface effect. XPS results showed that predominant species at surface layers of Co3O4 nanocrystals are octahedral Co (Ⅲ).
A new citrate acid-hydrazine sol-gel route for preparation of Co3O4 nanoparticles has been developed. Co3O4 nanoparticles with different particle-sizes and morphology were prepared at different heat-treatment temperatures and pure cubic nanocrystals of Co3O4 were obtained at 600 ° C. The synthesis structure was monitored by infrared spectroscopy (IR), thermal gravimetric and differential thermal analysis (TG-DTA). The structure and morphology of Co3O4 nanocrystals were characterized by X-ray powder diffraction (XRD) -ray-photoelectron spectroscopy (XPS). The infrared absorption bands blue-shifted with particle size decreasing, which could be attributed to increasing surface effect. XPS results showed that predominant species at surface layers of Co3O4 nanocrystals are octahedral Co (III).