We investigated the transport properties of isoelectronic substitution of Yb by Ca for Zintl phase YbCd2Sb2 below 300 K.The p-type Yb1-xCaxCd2Sb2(0.2≤x≤0.8)sa
【机 构】
:
Key Laboratory of Transparent Opto-Functional Inorganic Materials of Chinese Academy of Sciences,Gra
论文部分内容阅读
We investigated the transport properties of isoelectronic substitution of Yb by Ca for Zintl phase YbCd2Sb2 below 300 K.The p-type Yb1-xCaxCd2Sb2(0.2≤x≤0.8)samples were synthesized via a solid-state reaction followed by suitable cooling,annealing,grinding,and spark plasma sintering(SPS)densification processes.For samples with x=0.2,0.4,0.5,0.6,0.8,the electrical conductivity,Seebeck coefficient,thermal conductivity,heat capacity and Hall effect measurements were carried out in the temperature range from 1.9 to 300 K.It was found that the Ca substitution effectively lowered the thermal conductivity at low temperature,while the electrical resistivity and the Seebeck coefficient in the compounds were found to increase with increasing Ca concentration.As a result,the dimensionless figure of merit ZT of0.18 was attained at 300 K for sample with x=0.2.
其他文献
Extensive testing was carried out to study the effects of rare earth Ce doping on the properties of SnAgCu solder alloys. The addition of 0.03% (mass fraction)
It is economically advantageous to cast wrought aluminum alloys directly into near-net-shape components. The objective of the present work is to take advantage
The influence of the manganese-alloying on the structure and magnetocaloric properties of the Gd5Si2.05Ge1.95 compound was studied by X-ray powder diffraction a
Ce-doped ZnO films were prepared by the sol-gel method with spin coating onto glass substrates.Zinc acetate dihydrate,ethanol,diethanolamine and cerium nitrate
The cross-sectional distortion usually appears during rotary-draw bending process of thin-walled rectangular tube with small bending radius. To study the cross-
Ce-Cu-O monolithic catalysts were prepared by using Ce0.9Cu0.101.9 solid solution or nitrate as precursors,and their catalytic performance for the combustion of
Using solid-state synthesis method,a series of samples of lanthanum doped Li1-xLaxFePO4(x=0.0025,0.005,0.0075,0.01)were prepared.Each cathode structural and ele
In order to obtain the thermodynamic description of the Mg-Ga binary system, the thermodynamic assessment of the system was carried out using the CALPHAD method
The microstructure and properties of the 93W-4Ni-2Co-1Fe (mass fraction, %) tungsten heavy alloys prepared by mechanical alloying and electric current activated
With the development of aero-engine,gas import temperatures of hot section structural materials are increasingly higher.Metal alloy materials due to the rapidly