Carbon nanotube-reinforced 2009Al(CNT/2009Al) composites with randomly oriented CNTs and aligned CNTs were fabricated by friction stir processing(FSP) and FSP-rolling, respectively. The CNT/2009 Al composites with aligned CNTs showed much better tensile properties at room temperature and elevated temperature compared with those with the randomly oriented CNTs, which is mainly attributed to larger equivalent aspect ratio of the CNTs and avoidance of preferential fracture problems. However, much finer grain size was not beneficial to obtaining high strength above473 K. The aligned CNTs resulted in tensile anisotropy, with the best tensile properties being achieved along the direction of CNT aligning. As the off-axis angle increased, the tensile properties were reduced due to the weakening of the load transfer ability. Furthermore, aligned CNTs resulted in much lower coefficient of thermal expansion compared with randomly oriented CNTs.
CNT / 2009Al composites with aligned CNTs showed much better tensile properties at room temperature and elevated temperature compared with those with randomly oriented CNTs, which is mainly attributed to larger equivalent aspect ratio of the CNTs and avoidance of preferential fracture problems. However, much finer grain size was not profitable to obtain high strength above473 K. The aligned CNTs resulted in tensile anisotropy, with the best tensile properties being achieved along the direction of CNT aligning. lower coefficient of thermal expansion compared with randomly oriented CNTs.