热处理对AE42压铸镁合金低周疲劳行为的影响

来源 :特种铸造及有色合金 | 被引量 : 0次 | 上传用户:koptity
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
研究了固溶+时效处理(T6)对AE42压铸镁合金在疲劳加载条件下的循环应力响应行为、疲劳寿命以及断裂行为的影响。结果表明,压铸态和固溶+时效态的AE42镁合金均表现为循环应变硬化,固溶+时效处理可导致AE42压铸镁合金的循环应力幅有所提高,并可有效提高AE42压铸镁合金的疲劳寿命。疲劳断口形貌观察结果表明,疲劳裂纹萌生于疲劳试样的表面,并以穿晶方式扩展。 The effects of solution treatment and aging treatment (T6) on cyclic stress response behavior, fatigue life and fracture behavior of AE42 die-cast magnesium alloy under fatigue loading were studied. The results show that the AE42 magnesium alloys under both die casting and solid solution + aging behave as cyclic strain hardening. The solid solution and aging treatment can increase the cyclic stress amplitude of AE42 die-cast magnesium alloy and improve the wear resistance of AE42 die-cast magnesium alloy Fatigue life. Fatigue fracture morphology observations show that the fatigue crack initiation occurs on the surface of the fatigue specimen and propagates in a transgranular fashion.
其他文献
目的评估MR灌注参数(K~(trans))和扩散参数(ADC)在不同脑肿瘤的相关关系。方法回顾性研究13例脑肿瘤(男8例女5例平均年龄54.6±17.7岁,其中胶质母细胞瘤3例,低级别-间变性胶
目的 探讨人着色性干皮病基因D(xeroderma pigmentosum group D,XPD)和PPARγ对HepG2增殖及ERG表达的影响.方法 用脂质体转染法瞬时转染重组质粒pEGFP-N2/XPD和空载质粒pEGF
NeuN作为神经元的标志,是一种神经组织特异的蛋白,可能参与神经系统的发育、分化和功能,但是其具体作用机制还不清楚.目前Neun在神经系统发育、病理诊断以及神经元退化、坏死
目的 探讨XPD-751位点基因多态性与肝癌易感性的关系.方法 计算机检索CBM、CNKI、WANFANG DATA、VIP、Pubmed、Ovid等数据库,收集有关中国人群XPD-751位点基因多态性与肝癌易
缝隙连接在听觉功能中扮演了一个非常重要的角色。GJB2基因变异是一个导致~50%儿童单纯性耳聋的常见原因。此类基因变异产生的病理变化主要发生在耳蜗,然而听觉毛细胞上并无缝隙
目的 探讨EGF对体外培养POAG小梁网细胞增殖和凋亡的影响.方法体外培养POAG小梁网细胞并鉴定;用终浓度为0,5,10,20,50,100 ng/ml的EGF干预48 h,运用CCK-8比色法检测其吸光度
目的 探讨HBx(hepatitis B virus X protein)及HBs(hepatitis B virus S protein)对RhoC启动子的作用机制,分析可能相互作用的启动子调控元件.方法构建RhoC启动子截短突变克
在口腔临床工作中,重度磨损、低(牙合)龈距磨牙牙体缺损的修复一直是备受关注的难题.对于低(牙合)龈距磨牙牙体缺损的患者该如何设计、修复,相关基础研究较少,在临床修复时更
在无线Mesh网络(WMN)媒体访问控制(MAC)层上,分层信标帧驱动协议(Layer-BLBP)存在高延迟、多次重传以及无法适应较大规模拓扑结构的问题.为此,提出一种基于码片标识的WMN MAC
使用标准的齿条形刀具加工变齿厚齿轮,会造成变齿厚齿轮轮齿的左右侧端面压力角、螺旋角的变化和不等,影响两相交轴变齿厚齿轮的正确啮合,因此有必要研制非对称滚刀和调整机