以不同的硅源分别合成了L型沸石,考察了影响L型沸石晶化相区的各种因素。首次发现了L型沸石导向刑,并对其导向作用进行了研究。
L - type zeolites were synthesized from different silicon sources respectively, and various factors influencing the crystallization phase of L - type zeolites were investigated. For the first time, the L-type zeolite was found to be the target of punishment and its orientation was studied.