Conicraly相关论文
本文研究了真空热处理后的APS-CoNiCrAlY+APS-YSZ 和HVOF-CoNiCrAlY+APS-YSZ 热障涂层系统在室温-1050℃ 环境中的100-h 热循环行......
为了提高Al2O3/CoNiCrAlY涂层的抗高温氧化能力,采用激光熔覆的方法在K438合金的表面制备Al2O3/CoNiCrAlY涂层,并研究不同的能量密......
为了解决曹娥江大闸期启闭机活塞杆的磨损问题,利用高焓等离子喷涂技术制备黏结层为CoNiCrAlY,面层为Cr2O3·5SiO2·3TiO2的梯度陶......
Influence of Heat Treatment on the Bond Coat Cyclic Oxidation Behaviour in an Air-plasma-sprayed The
It is generally believed that a thermally grown oxide (TGO) layer of alumina provides enhanced protection to the metalli......
Microstructural evolution and growth kinetics of thermally grown oxides in plasma sprayed thermal ba
为探究吕家坨井田地质构造格局,根据钻孔勘探资料,采用分形理论和趋势面分析方法,研究了井田7......
Influence of Heat Treatment on the Bond Coat Cyclic Oxidation Behaviour in an Air-plasma-sprayed The
It is generally believed that a thermally grown oxide (TGO) layer of alumina provides enhanced protection to the metalli......
To improve the durability of underwater rotating products,the corrosion characteristics in harsh marine environment were......
据《Теплоэнерrетика》2007年2月号报道，俄罗斯ЦКТН（中央锅炉涡轮机研究所）研究了CoNiCrAlY系合金元素对燃气轮机......
The corrosion behavior of High-Velocity Oxygen Fuel (HVOF) sprayed MCrAlY coatings obtained from CoNiCrAlY particles (wt......
The corrosion behavior of High-Velocity Oxygen Fuel (HVOF) sprayed MCrAlY coatings obtained from CoNiCrAlY particles (wt......
热障涂层由具有隔热作用的陶瓷涂层和起粘结作用的金属粘结层组成,其中金属粘结层为MCrAlY(M=Ni,Co或Ni-Co),起到改善陶瓷涂层和基......
Influence of Heat Treatment on the Bond Coat Cyclic Oxidation Behaviour in an Air-plasma-sprayed The
It is generally believed that a thermally grown oxide (TGO) layer of alumina provides enhanced protection to the metalli......
利用等离子喷涂法在TiAl合金基体表面依次喷涂结合紧密的过渡CoNiCrAlY涂层和(ZrO2+Y2O3)的陶瓷热障涂层,并进行高温氧化试验.用XR......
利用行星球磨技术制备了纳米结构CoNiCrAlY粉末,采用XRD,SEM等方法对传统结构粉末和纳米结构粉末在1 000℃时的氧化行为进行了研究......
采用气雾化技术制备了CoNiCrAlY合金粉末,同时对合金熔炼过程中的成分变化,雾化参数对粉末的粒度、形貌和微观组织进行了分析研究......
高温服役过程中热障涂层的MCrAlY粘结层形成致密的氧化铝层,从而提高了涂层和基体的抗氧化性能.利用等离子喷涂制备的热障涂层,其......
用等离子喷涂法在TiAl合金基体表面依次喷涂CoNiCrAlY涂层和(ZrO2+Y2O3)陶瓷障涂层,对处理后的TiAl合金进行高温氧化试验,结果表明......