EAF-LF-VD相关论文
对 30 t EAF- L F- VD冶炼高级齿轮钢的过程进行分析 ,由此确定 L F- VD过程中的成分微调工艺和 VD过程中成分的变化规律 ,并对钢......
对30tEAF-LF-VD冶炼高级齿轮钢的过程进行分析,由此确定LF-VD过程中的成分微调工艺和VD过程中成分的变化规律,并对钢的各项性能与化学成分进行逐步回归分......
34CrNiMo6钢(/%:0.30~0.38C,0.50~0.80Mn,≤0.40Si,0.015~0.035S,≤0.035P,1.30~1.70Ni,1.30~1.70Cr,0.15~0.30Mo)的冶金流程为30 t E......
试验14Cr1Mo钢(/%:0.12C,0.57Si,0.48Mn,0.003P,0.001S,1.20Cr,0.42Mo,0.01V,0.001Nb,0.017A1,0.003As,0.001 Sb,0.002Sn)64 mm×......
在UHP EAF-LF-VD-IC轴承钢的生产线上,对影响轴承钢氧含量的主要因素如脱氧剂、脱氧方式、精炼炉渣、温度制度、吹氩强度等进行了探......
通过对石油钻杆接头用钢37CrMnMo冶炼过程现场取样,对试样中的夹杂物进行定量和定性分析,确定了该钢种夹杂物控制改进措施.轧材中......
含钛钢冶炼采用钛铁、钛线合金化冶炼实践及热力学分析表明,钛的氧化反应造成钛收得率降低,钢液中一定的Al含量可提高钛收得率。通......
生产的高压锅炉用钢SA-210A1(/%:0.08~0.11C,0.22~0.24Si,0.72~0.74Mn,0.007~0.010P,0.004~0.005S,0.010~0.015V,0.025~0.035Ti,0.012~0.018A......