ECSTM相关论文
The adsorption of a variety of fullerenes (C60,C70,C86,Y@C82) on Au(111) electrode surfaces was comprehensively investig......
电化学扫描隧道显微镜(ECSTM)因其能提供真实空间的原子分辨图象而成为现场研究电极表面结构的最强有力的手段之一。近来,欠电位......
Electrochemical Scanning TUnneling Microscopy (ECSTM) has been extended to characterizc polycrystalline silver electrode......
研究发现当电极电位处于双层区时,三种分子在Au(111)电极表面均可形成高度有序的吸附结构.TTF与TCNQ分子有序吸附层的单胞结构分别......
A nanocrystalline coating of Cu-20Zr (in wt pct) was obtained on glass by magnetron sputtering. The corrosion behavior o......
采用“二步包封”法制备了性能良好的电化学STM针尖.以此为基础采用ECSTM现场研究了工艺条件下HOPG上高择优锌-镍合金的电沉积过程.研究结果表明这......
本文综述了扫描隧道显微镜(STM)以及现场电化学扫描隧道显微镜(ECSTM)探针的制备方法,并对相应探针制备方法的优缺点以及探针性能......
...
利用电化学扫描隧道显微镜(ECSTM)在温和的电化学和隧道偏压的条件下诱导电极表面发生特定的局域电化学反应,在Au(u1)单晶电极表面......
A nanocrystalline coating of Cu-20Zr (in wt pct) was obtained on glass by magnetron sputtering. The corrosion behavior o......
采用0.001mol/LCuSO4+0.5mol/LH2SO4溶液体系,在Pt单晶球电极作循环伏安曲线,得到 Cu存在欠电位沉积和本体沉积两个阶段,利用电化学扫描隧道显微观察到在欠电位下......
利用电化学扫描隧道显微镜(ECSTM)现场观察Co、Cu在铂单晶(111)面上的电结晶成膜过程.结果表明:Cu在铂单晶(111)面上的电结晶过程......
本文利用扫描隧道显微镜及自制的无源恒电位仪组成电化学扫描隧道显微镜(ECSTM),对浸泡在0.5mol/L H2SO4+0.02mol/L NaCl 溶液中的......
<正> 电化学扫描隧道显微镜(ECSTM)因其能提供真实空间的原子分辨图象而成为现场研究电极表面结构的最强有力的手段之一。近来,欠......
<正> 电聚吡咯过程机理的研究,多年来由于仪器的限制仅限于从间接的方式获得证据,为了得到溶液中真实的电聚吡咯过程信息,我们用自......
采用“二步包封”法制备了性能良好的电化学STM针尖。以此为基础采用ECSTM现场研究了工艺条件下HOPG上高择优锌-镍合金的电沉积过程。研究结果表......
以喷金云母片为基体,浓度为正常镀液5%的电镀镍液作母液,应用电化学扫描隧道显微镜在纳米尺度范围内在线原位观察光亮剂对镀层微观形......
用自制的电化学扫描隧道显微镜(ECSTM)现场研究Cu在HOPG上的电沉积过程.结果表明Cu在HOPG上的电沉积为三维成核的过程.当电位较低或Cu2+离子浓度较低时,铜在本......
用自制的电化学扫描隧道显微镜(ECSTM)现场研究Cu在HOPG上的电沉积过程.结果表明Cu在HOPG上的电沉积为三维成核的过程.当电位较低或Cu2+离子浓度较低时,铜在本......