The shear viscosity bound violation in Einstein gravity for anisotropic black branes is discussed, with the aim of const......
在温度623~923 K下采用真空热压扩散连接铝和铜,具体工艺为在预置温度下,变形率为0.2 mm/min时热压缩10 min,再在炉冷过程中,以0.2 ......
采用等离子活化烧结方法实现了Cu箔和Al箔的固相扩散结合,考察了673~773K温度范围内界面金属间化合物(IMCs)层的生成过程和生长动力......
The elevated temperature tensile experiments have been carried out on the magnesium alloy and results indicate that the ......
The vacuum diffusion bonding of titanium alloy to tin-bronze has been studied and the feasibility and appropriate proces......
In this study, intermetallic TiAl and steel 40Cr are diffusion bonded successfully by using a composite barrien layer Ti......
采用粉末冶金法制备了钨钼复合双金属靶材,研究了不同工艺参数下复合材料的界面组织和结构。试验结果表明,控制适当工艺参数可以获......
与涂层,这被称为以铝覆盖之渗铬的 Cr-modifiedaluminide 涂层和做 Y 的铬的二种不同类型在 600 合金是涂的这被称为 aluminizing-c......
Superplastic forming and diffusion bonding (SPF/DB) is a well-established process for the manufacture of components almo......
A new diffusion bonding technique combined with laser cladding process was developed to join TiAl alloy to itself and Ti......
Field-assisted diffusion bonding applied in the joining of solid electrolyte borosilicate glass, β″-Al2O3, Y2O-ZrO2 to......
An ultrasonic evaluation method of echo feature of diffusion bond joint between two dissimilar materials is presented. T......
...
在温度623~923K下采用真空热压扩散连接铝和铜,具体工艺为在预置温度下,变形率为0.2mm/min时热压缩10min,再在炉冷过程中,以0.2mm/......
日本一所大学的专家研究成功一种在空气中就能使陶瓷材料和耐热金属(如钛、铝等)结合的方法.过去采用的方法是在真空中将一种氧化......
将用一个侧冒口补缩两个锤头,改为顶冒口,一个冒口补缩一个锤头。通过扫描电镜、能谱分析,对硬质合金-超高锰钢结合区的显微组织、化......
探讨了包覆焊接一拉拔法铜包铝线在拉拔工序中实现“金属键合”和退火加热工序中实现“扩散结合”的机理。研究了界面上脆性氧化膜......
介绍一种用于液体与制冷工质进行热交换的集成式微通道换热器。经测试,该换热器在满足压力损失限制和耐压性能的条件下,其强制对流换......
采用磁控溅射法制备出HA/YSZ/Ti6Al4V生物复合材料,利用X-射线衍射仪(XRD)、扫描电镜(SEM)和能谱分析(EDXA)研究复合涂层的相组成、表面微观......
在不同的热处理工艺下,生产出高锰钢复合材料。通过扫描电镜对高锰钢、陶瓷复合材料的结合情况、基体的显微组织进行了研究,并探讨......