论文部分内容阅读
The C15 Laves phase with composition Tb0.2Pr0.8(Fe0.4Co0.6)1.93 was synthesized by mechanical alloying (MA) and subsequent annealing process. The structure and magnetic properties of Tb0.2Pr0.8(Fe0.4Co0.6)1.93 were investigated by means of X-ray diffraction (XRD), a vibrating sample magnetometer, and a standard strain technique. The effect of annealing on the structure and magnetic properties was studied. The analysis of XRD shows that the high Pr-content Tb0.2Pr0.8(Fe0.4Co0.6)1.93 alloy with the single phase of MgCu2-type structure can be success-fully synthesized by MA method. The sample annealed at 450℃ is fotmd to have a coercivity of 196 kA/m at room temperature. An ep-oxy/Tb0.2Pr0.8(Fe0.4Co0.6)1.93 composite was produced by a cold isostatic pressing technique. A large magnetostriction of 400 ppm, at an ap-plied magnetic field of 800 kA/m, was found for the composite. The epoxy-bonded Tb0.2Pr0.8(Fe0.4Co0.6)1.93 composite combines a high mag-netostriction with a significant coereivity, which is a promising magnetostrictive material.