Influence of Charge Density and Chain Length on the Interaction between Organic Anion and Montmorill
【机 构】
:
Tianjin Key Laboratory of Composite and Functional Materials, School of Materials Science and Engine
【出 处】
:
武汉理工大学学报(材料科学版)(英文版)
【发表日期】
:
2013年1期
其他文献
An attempt was made to investigate the machinability of SiCp/Al composites based on the experimental study using mill-grinding processing method. The experiments were carried out on a high-speed CNC machining center using integrated abrasive cutting tool.
Effect of Hydration Aging and Water Binder Ratio on Microstructure and Mechanical Properties of Spra
In order to study the durability of sprayed concrete (shotcrete), effects of different hydration aging and water-binder ratio (w/b) on the microstructure of cement paste and basic mechanical properties of test specimens were investigated. The phase compos
Wear resistances of CO2 corrosion product iflms formed on P110 carbon steel at different CO2 partial pressures were investigated in water sand two-phase lfow by weight loss method, and the microstructures and compositions of corrosion product iflms were a
A plasticizer triethylene glycol maleate (TEG-MA) was synthesized. The dominated monoester of moderate hydrophobicity with apparent oil-water partition coefifcient of 0.042 in the product was conifrmed by acid value determination, HPLC and FTIR. Its plast
Water-conducting Characteristics and Micro-dynamic Self-adjusting Behavior of Polyacrylamide/Montmor
A water-conducting polyacrylamide/montmorillonite coating was prepared by solution-blending. The coating was coated on fiber and then composited with polymer to form a composite film material that used for water saving and tree planting in arid and desert
Based on the erosion resistant coefficient, the effects of water-cement ratio, air-entrained, silica fume content and sand ratio on the sulfate attack resistance of air-entrained silica fume concrete were studied by orthogonal experiments in order to expl
Adopting a ceramic/polymer multilayer structure design to simulate the structure of nacre is usually believed to be an effective way to increase the toughness of ceramic composites at the expense of the material\'s bending strength. However, in this stu
Using the oxidation method from vanadium metal thin films by magnetron sputtering, under the fixed annealing parameters of temperature (400℃) and oxygen pressure (103 Pa), we fabricated a series of vanadium dioxide thin films through the change of anneali