The molten eutectic mixture of magnesium,sodium and potassium chlorides(Mg Cl2–Na Cl–KCl) has inappreciable solubility for oxide ions,and can help disengage a carbon anode from the oxide ions generated at a metal oxide cathode,and effectively avoid carbon dioxide formation.This “disengaging strategy” was successfully demonstrated in electro-reduction of solid oxides of zirconium and tantalum.It has led to significantly higher current efficiency(93%),and lower energy consumption(1.4 k W h kg 1) in electrolysis of tantalum oxide to tantalum metal compared to the conventional electrolysis in molten calcium chloride(e.g.78% and 2.4 k W h/kg-Ta).
The molten eutectic mixture of magnesium, sodium and potassium chlorides (Mg Cl2-Na Cl-KCl) has inappreciable solubility for oxide ions, and can help disengage a carbon anode from the oxide ions generated at a metal oxide cathode, and effectively avoid carbon dioxide formation. This “disengaging strategy” was successfully demonstrated in electro-reduction of solid oxides of zirconium and tantalum. It has led to significantly higher current efficiency (93%), and lower energy consumption (1.4 k W h kg 1) in electrolysis of tantalum oxide to tantalum metal compared to the conventional electrolysis in molten calcium chloride (eg78% and 2.4 k W h / kg-Ta).