The initial temper of the material may directly affect the whole creep age forming(CAF)process. In terms of creep deformation and stress relaxation, using the constant-stress creep aging and constant-strain stress relaxation aging tests, the relationship between initial temper and CAF formability is investigated for an Al-Zn-Mg-Cu alloy at 165 °C for 18 h. Three tempers are selected as the initial tempers in CAF, viz., solution, retrogression and re-solution. The CAF formability of this alloy with initial temper of retrogression is the best, and the creep strain of the retrogression tempered specimen after creep aging of 18 h is about 1.21 and 1.34 times than that of the solution and the re-solution tempered specimens, respectively. The calculated stress exponents of this alloy with three initial tempers range from 7.3 to 9.5, indicating that the CAF of this alloy is mainly controlled by the dislocation creep. The various formability for three initial tempers are attributed to different inhibitions of the transgranular precipitates on the dislocation movement. For the retrogression temper, the initial fine and uniformly distributed precipitates are seriously coarsened after6 h of CAF, which minimally inhibit the dislocation movement. While, for the re-solution temper,the fine precipitates are re-precipitated in the matrix of the alloy, which observably hinder the dislocation movement and lead to the worst formability. The initial temper of the material may directly affect the whole creep aging forming (CAF) process. In terms of creep deformation and stress relaxation, using the constant-stress creep aging and constant-strain stress relaxation aging tests, the relationship between initial temper and CAF formability is investigated for an Al-Zn-Mg-Cu alloy at 165 ° C for 18 h. Three tempers are selected as the initial tempers in CAF, viz., Solution, retrogression and re-solution. The CAF formability of this alloy with initial temper of retrogression is the best, and the creep strain of the retrogression tempered specimen after creep aging of 18 h is about 1.21 and 1.34 times than that of the solution and the re-solution tempered specimens, respectively. The calculated stress exponents of this alloy with three initial tempers range from 7.3 to 9.5, indicating that the CAF of this alloy is mainly controlled by the dislocation creep. The formations for three initial tempers are attributed to differe nt inhibitions of the transgranular precipitates on the dislocation movement. For the retrogression temper, the initial fine and uniformly distributed precipitates are serious coarsened after 6 h of CAF, which minimally inhibit the dislocation movement. While, for the re-solution temper, the fine precipitates are re-precipitated in the matrix of the alloy, which observably hinder the dislocation movement and lead to the worst formability.