对高韧性管线用钢控轧控冷工艺制度、力能参数和产品质量的控制进行了测定、研究，并得出，此种管线用钢的轧制工艺制度为，出炉温度在１１５０℃左右，终轧温度为８００℃左右，卷取温度为６００℃左右，加速冷却速度为１５℃／Ｓ左右。
The toughness of the pipeline steel with controlled rolling and controlled cooling process system, power parameters and product quality control were measured and studied, and concluded that such pipeline steel rolling process system, the baked temperature at about 1150 ℃, The finishing temperature is about 800 ℃, the coiling temperature is about 600 ℃, and the accelerated cooling rate is about 15 ℃ / S.