【摘 要】
：
应用Gleeble3800热模拟试验机测试了Q345E钢连铸坯的高温力学性能,通过观察试样断口形貌分析变形断裂机理。试验结果表明:在600~1 300℃范围内Q345E钢的脆性温度区间为750~90
论文部分内容阅读
应用Gleeble3800热模拟试验机测试了Q345E钢连铸坯的高温力学性能,通过观察试样断口形貌分析变形断裂机理。试验结果表明:在600~1 300℃范围内Q345E钢的脆性温度区间为750~900℃,塑性温度区间为950~1 300℃,为指导Q345E钢的连铸生产提供理论依据。
The high temperature mechanical properties of Q345E steel continuous casting slab were tested by Gleeble3800 thermal simulation test machine. The fracture mechanism of the Q345E steel continuous casting slab was analyzed by observing the fracture surface morphology. The experimental results show that the brittleness temperature range of Q345E steel is from 750 ℃ to 900 ℃ and the plastic temperature range is from 950 ℃ to 1 300 ℃ in the range of 600 ℃ to 1 300 ℃, providing the theoretical basis for guiding the continuous casting of Q345E steel.
其他文献
“2000年中国建筑智能化论坛”来自国内外的建筑智能化方面的专家、学者在会上作了高水平的专题报告，对国内外建筑智能化技术的热点问题进行了研讨，受到与会者的欢迎。本次论坛
以水银和氩气作为模拟介质,通过物理模拟研究了高拉速板坯连铸结晶器内电磁制动和水口吹氩耦合作用下的气泡运动和分布行为.采用电阻探针测量了结晶器内气泡的运动和分布情况
例1:男,72岁,9天前因左手中指外伤后患破伤风于1992年7月28日入院。体检:患者呈苦笑面容,张口约lcm,左手中指有1.5cm愈合伤口,末节轻度肿胀,按压伤口及强声刺激可引起全身阵
泪腺结核１例浙江省绍兴市第四医院３１２００７朱金元病人女６９岁教师。１９９２年６月因右眶上肿胀３个月及眶下皮下硬结，就诊于本院眼科。初诊为泪腺炎症，肿瘤待除外，行抗炎治疗半月无效。同年７月，先后行ＣＴ及核
根据120例人体内外胆囊结石的CT4种密度分类和CT 值测试与化学成分的定性和定量分析对比表明:高密度者属胆色素钙类石;低、等密度者属胆固醇类石;混合密度者属混合类石.其中
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
急性华支睾吸虫病一例报告广西中医学院南宁５３０００１蔡美秋广西医科大学南宁５３００２７黄若密患者男性，４０岁，南宁市人。因恶寒、发热伴腹痛半个月，于１９９２年１２月２６日就诊。半月来，患者出现不规则恶寒，发热，体温最
为了预防结核病的发生，从1987年以来，对我院连续五届人学新生，凡在预防接种时发现结核菌素试验（下称结素）强阳性反应者，都给予严格的预防投药治疗并收到了一定的效果。体会到这一预
考虑了化学反应及压力梯度力,对等离子喷涂流场分布及颗粒运动特性进行研究。利用Spray Watch-2i对飞行颗粒进行在线监测。结果表明:气流的最高温度为12000 K,最高速度为150
新型隐球菌脑膜炎临床表现复杂,极易误诊。本实验室自1998年3月至2000年10月间共检出5例此病,现报告如下。 1 临床资料本文5例中男3例,女2例,年龄9～57岁。住院病人2例,门诊病