对15%、20%冷加工和固溶态的三种状态含钛316不锈钢在不同温度和应力下进行了蠕变断裂试验。结果表明,从600℃开始,冷加工材料断裂塑性随试验温度增加
Creep rupture test was carried out on Ti-containing 316 stainless steel in 15%, 20% cold-working and solid-solution states at different temperatures and stresses. The results show that starting from 600 ℃, the plasticity of cold working material increases with the increase of test temperature