The effect of hot finishing rolling temperature on cube texture in high purity aluminium foils was investigated by means of orientation distribution functions (ODFs). The results show that a relatively strong rotated cube orientation ｛100｝〈011〉 exists when the end temperature of hot finishing rolling is 290 ℃, and the cube texture is the strongest after the final recrystallization. The cold rolling textures are comprised of S? , Cu and Bs components, and the orientation ｛100｝〈011〉 is unstable, it may be split and evolved into two complementary copper components (112) [1—1—1] and (1—1—2) [111] during the cold rolling. And a sharp cube recrystallization texture would nucleate and grow in the deformation matrix with the Cu orientation. [ The results of hot finishing rolling temperature on cube texture in high purity aluminum foils was investigated by means of orientation distribution functions (ODFs). The results show that a relatively strong rotated cube orientation {100} <011> exists when the end temperature of hot finishing rolling is 290 ° C, and the cube texture is the strongest after the final recrystallization. The cold rolling textures are comprised of S ?, Cu and Bs components, and the orientation {100} <011> is unstable, it may be split and evolved into two complementary copper components (112) [1-1-1] and (1-1-2) [111] during the cold rolling. And a sharp cube recrystallization texture would nucleate and grow in the deformation matrix with the Cu orientation . [