Bulk Sm2Fe17Nx sintering magnet was fabricated by spark plasma sintering(SPS) technique. The effects of sintering pressure and sintering temperature on the magn
【机 构】
：
Key Laboratory of Advanced Functional Materials
论文部分内容阅读
Bulk Sm2Fe17Nx sintering magnet was fabricated by spark plasma sintering(SPS) technique. The effects of sintering pressure and sintering temperature on the magnetic properties of the Sm2Fe17Nx magnet were investigated. As a result, the density of the magnet is obviously improved with the increase of sintering pressure, but the coercivity drops since Sm2Fe17Nx has decomposed into SmN, α-Fe and N2. When sintering temperature was only above 200 ℃ under 1 GPa sintering pressure, the coercivity even begins to decrease, which indicates that high pressure promotes the decomposition of the Sm2Fe17Nx at lower temperature. The decomposition is also proved by the decrease of nitrogen and increase of α-Fe in the magnets.
其他文献
The microstructural evolution of cold-rolled aluminum alloy 3003 during annealing was investigated by means of micro-hardness measurement, electrical resistivit
A series of new microwave dielectric ceramics Ba3-nLa1+nTinNb3-nO12 (n=0,1,2) were prepared in the BaO-La2O3-TiO2-Nb2O5 system by high temperature solid-state r
The microstructures of the AZ91D die-cast magnesium alloy were investigated by scanning electron microscopy (SEM), X-ray diffractometry (XRD) and energy dispers
Based on the heat transfer theory and liquid solidification theory, the heat transfer during the rapid solidification process of amorphous ribbons prepared by m
The vesicant problem during the process of preparing closed-cell aluminum foam by molten body transitional foaming process was discussed and the effect of granu
A stable δ- and β-bismuth trioxide was prepared at room temperature by vacuum vapor-phase oxidation. The average crystal size of products was 14.6 nm (by XRD)
SiCp/Gr/2024Al metal matrix composites were processed by squeeze casting technology. The microstructure of composites was observed by SEM and TEM, and the effec
This research indicates that the gradient of internal relative humidity (IRH) decreases rapidly within 7-day curing age in HPC.The amount of water imported by p
Twin-roll thin strip casting process combines casting and hot rolling into a single process,in which thermal stress and thermal mechanical stress were involved.
Comparing with that of low-calcium fly ash (LF) or fly dreg (FD), chemical content of high-calcium fly ash (HF) waves more much. Coarse grain, which existing in