Dynamic rheological properties of asphalt modified by Supramolecular UV resistant material-layered double hydroxides(LDHs) was studied by means of the dynamic shear rheometer(DSR) test.Two typical base asphalts were chosen and modified by 2 different LDHs contents.DSR tests were performed on the original samples,samples after exposed to outdoor and samples after the artificial accelerated UV aging tests respectively to analyze the rheological properties.It is found that when the LDHs content is between 3wt% and 5wt% of asphalt weight,the high temperature performance and fatigue resistant property of the modified asphalt become better,the UV aging resistance properties are improved.
Dynamic rheological properties of asphalt modified by Supramolecular UV resistant material-layered double hydroxides (LDHs) were studied by means of the dynamic shear rheometer (DSR) test. Two typical base asphalts were chosen and modified by 2 different LDHs contents. DSR tests were performed on the original samples, samples after exposed to outdoor and samples after the artificial accelerated UV aging tests respectively to analyze the rheological properties. It is found that when the LDHs content is between 3 wt% and 5 wt% of asphalt weight, the high temperature performance and Fatigue resistant property of the modified asphalt become better, the UV aging resistance properties are improved.