论文部分内容阅读
By using a whitelight lamp, an Ar+ ion laser whosewavelength was tuned to 457. 9 nmand a tunable Rh 6G dye laser(linewidth: 0. 5 cm-1) pumped bythe second harmonic of a Nd: YAGlaser as light sources and using amonochromator, a phase-lockingamplifier and a computer as the data detecting system, the transmission spectrum, fluorescence spectra, excitation spectrum and siteselective fluorescence spectra ofthe Eu3+: Y2SiO5 crystal were observed. More than thirty out of thetotal fifty spectral lines were observed for 5D0→7F0,1,2,3,4 transitions. The Eu3+ ions occupy twokinds of the Y3+ sites with the lowsymmetry in this crystal. The difference of the wavelengths of thetwo Eu3+ sites for 7F0→5D0 transition is about 0. 2 nm. It was foundthat the two sites were nonequivalent optical ones at room temperature. Crystal lattice constants a,b, c, and β of Eu3+: Y2SiO5 werealso measured by the X-ray diffraction method. The results show thatthe lattice constants a, b, and cof the crystal doped Eu3+ ions isvery close to those of the Y2SiO5crystal undoped Eu3+ ions.