摘要：混凝土结构裂缝是当今工程领域难以解决又较普遍存在的问题，如果施工中混凝土常常出现裂缝就会影响到结构的整体性和耐久性。结合实际经验，从建筑构件、温度变化、体积收缩和施工操作等方面分析了施工期混凝土裂缝产生原因和影响因素，提出了施工期混凝土裂缝的控制技术，对在如何进行混凝土裂缝控制的研究和实践有一定的指导意义。
关键词：混凝土；裂缝成因；防治措施
Abstract: the concrete crack is the engineering field and is difficult to solve common problems, if the construction of concrete cracks often will affect the structure integrity and durability. Combined with practical experience, from the construction component, change of temperature, volume contraction and construction operation, analyzes the concrete crack during the reason and influence factors, put forward the concrete cracks during the control technology, in how to carry on the concrete to crack control of research and practice have some guiding significance.
Keywords: concrete; Crack is presented; Prevention and control measures
中图分类号： TU528 文献标识码：A 文章编号：
引言：下面就混凝土裂缝的成因与控制谈谈。
1.裂缝的成因
裂缝产生的形式和种类很多，要根本解决混凝土中裂缝问题，需要从混凝土裂缝的形成原因入手。正确判断和分析混凝土裂缝的成因是有效地控制和减少混凝土裂缝产生的最有效的途径。
1.1设计原因
1.1.1设计结构中的断面突变而产生的应力集中所产生的构件裂缝。
1.1.2设计中对构件施加预应力不当，造成构件的裂缝(偏心、应力过大等)。
1.1.3设计中构造钢筋配置过少或过粗等引起构件裂缝(如墙板、楼板)。
1.1.4设计中未充分考虑混凝土构件的收缩变形。
1.1.5设计中采用的混凝土等级过高，造成用灰量過大，对收缩不利。
1.2材料原因
1.2.1粗细集料含泥量过大，造成混凝土收缩增大。集料颗粒级配不良或采取不恰当的间断级配，容易造成混凝土收缩的增大，诱导裂缝的产生。
1.2.2骨料粒径越细、针片含量越大，混凝土单方用灰量、用水量增多，收缩量增大。
1.2.3混凝土外加剂、掺和料选择不当、或掺量不当，严重影响混凝土收缩。
1.2.4水泥品种原因，矿渣硅酸盐水泥收缩比普通硅酸盐水泥收缩大、粉煤灰及矾土水泥收缩值较小、快硬水泥收缩大。
1.2.5水泥等级及混凝土强度等级原因：水泥等级越高、细度越细、早强越高对混凝土开裂影响很大。混凝土设计强度等级越高，混凝土脆性越大、越易开裂。
1.3混凝土配合比设计原因
1.3.1设计中水泥等级或品种选用不当。
1.3.2配合比中水灰比(水胶比)过大。2009年，本人负责大江村民公寓工程现场监理工作，该工程在进行二层楼板砼的捣制时，由于混凝土搅拌站提供的混凝土出现水灰比比例调配不当，以致影响到混凝土的凝结期。由于发现及时，立即采取措施加强养护，加上养护妥当，使得该层楼板砼强度达到设计要求，不致造成返工。
1.3.3单方水泥用量越大、用水量越高，表现为水泥浆体积越大、坍落度越大，收缩越大。
1.3.4配合比设计中砂率、水灰比选择不当造成混凝土和易性偏差，导致混凝土离淅、泌水、保水性不良，增加收缩值。
1.3.5配合比设计中混凝土膨胀剂掺量选择不当。
1.4施工及现场养护原因
1.4.1现场浇捣混凝土时，振捣或插入不当，漏振、过振或振捣棒抽撤过快，均会影响混凝土的密实性和均匀性，诱导裂缝的产生。
1.4.2高空浇注混凝土，风速过大、烈日暴晒，混凝土收缩值大。
1.4.3对大体积混凝土工程，缺少两次抹面，易产生表面收缩裂缝。
1.4.4大体积混凝土浇注，对水化计算不准、现场混凝土降温及保温工作不到位，引起混凝土内部温度过高或内外温差过大，混凝土产生温度裂缝。
1.4.5现场养护措施不到位，混凝土早期脱水，引起收缩裂缝。
1.4.6现场模板拆除不当，引起拆模裂缝或拆模过早。
1.4.7现场预应力张拉不当(超张、偏心)，引起混凝土张拉裂缝。
2.裂缝的控制措施
2.1设计中的“抗”与“放”在建筑设计中应处理好构件中“抗”与“放”的关系
所谓‘抗’就是处于约束状态下的结构，没有足够的变形余地时，为防止裂缝所采取的有力措施，而所谓“放”就是结构完全处于自由变形无约束状态下，有足够变形余地时所采取的措施。设计中应尽量避免结构断面突变带来的应力集中。如因结构或造型方面原因等而不得以时，应充分考虑采用加强措施；积极采用补偿收缩混凝土技术：常见的混凝土裂缝中，有相当部分都是由于混凝土收缩而造成的。要解决由于收缩而产生的裂缝，可在混凝土中掺用膨胀剂来补偿混凝土的收缩，实践证明，效果是很好的。
2.2材料选择和混凝土配合比
设计方面根据结构的要求选择合适的混凝土强度等级及水泥品种、等级，尽量避免采用早强高的水泥；选用级配优良的砂、石原材料，含泥量应符合规范要求；积极采用掺合料和混凝土外加剂，可以降低水泥用量、降低水化热、改善混凝土的工作性能和降低混凝土成本的作用；正确掌握好混凝土补偿收缩技术的运用方法。对膨胀剂应充发考虑到不同品种、不同掺量所起到的不同膨胀效果。应通过大量的试验确定膨胀剂的最佳掺量；配合比设计人员应深入施工现场，依据施工现场的浇捣工艺、操作水平、构件截面等情况，合理选择好混凝土的设计坍落度，针对现场的砂、石原材料质量情况及时调整施工配合比，协助现场搞好构件的养护工作 。混凝土是非均质的三相体，即固体、液体和气体。两种相接触的面称为界面，混凝土中界面的存在是无法避免的，对混凝土性能产生不良影响。混凝土拌合物三相所占的体积大致为，固相占总体积的73%~84%、液相占15%~22%、气相占1%~5%。三相体积的改变是混凝土产生裂缝主要原因之一，尤其是混凝土产生终凝之前较为明显（即通常认为随行收缩，干燥收缩等引起的裂缝），但这种裂缝如果在浇筑后及时采取有效的养护措施，能够获得明显的控制效果。
2.2.1混凝土配合比除应按《普通混凝土配合比设计规程》JGJ55的规定，根据要求的强度等级、抗渗等级、耐久性及工作性等进行配合比设计外，其配制的混凝土还应符合4.3.2-4.3.10的规定。
2.2.2干缩率。混凝土90d的干缩率宜小于0.06%。
2.2.3坍落度。在满足施工要求的条件下，尽量采用较小的混凝土坍落度；基础、梁、楼板、屋面用的混凝土坍落度宜小于120mm，柱、墙用的混凝土坍落度宜小于150mm；混凝土采用泵送时，高层建筑用的混凝土坍落度根据泵送高度宜控制在180mm左右，多层及高层建筑底部的混凝土坍落度宜控制在150mm。
2.2.4用水量。不宜大于170kg/m3。
2.2.5水泥用量。普通强度等级的混凝土宜为270-450千克每立方米，高强混凝土不宜大于550千克每立方米。
2.2.6水胶比。应采用较小的水胶比。混凝土水胶比不可大于0.60。
2.2.7砂率。在满足工作性要求的前提下，应采用较小的砂率。
2.2.8宜采用引气剂或引气减水剂。
3.混凝土的养护
3.1养护是防止混凝土产生裂缝的重要措施，必须充分重视，并制定养护方案，派专人养护工作。2004年本人负责世纪嘉园项目的现场监理工作，该项目有1层8000多平方米的地下室，当进行地下室面板施工时，刚好六月初，天气较炎热，刚开始捣制地下室面板时，由于施工方养护措施不当，导致部分面板出现不同程度的裂缝，在发现上述问题后，项目监理部立即组织施工方开会分析原因：由于天气炎热养护不够造成开裂，立即制定落实养护措施，并要求施工方派专人定时负责养护，由于发现及时，加上后期养护措施得当，该地下室面板后期没有再出现裂缝，该例子充分体现混凝土养护的重要性。
3.2混凝土浇注完毕，在混凝土凝结后即须进行妥善的保温、保湿养护，尽量避免急剧变化、振动以及外力的扰动。
3.3浇筑后采用覆盖、晒水、喷雾或用薄膜保湿等养护措施；保温、保湿养护时间，对硅酸盐水泥、普通硅酸盐水泥或矿渣硅酸盐水泥拌制的混凝土，不得少于7d；对掺用缓凝型外加剂或抗渗要求的混凝土，不得少于14d。
3.4底板和楼板等平面结构构件，混凝土浇筑收浆和抹压后，用塑料薄膜覆盖，防止表面水份蒸发，混凝土硬化才可上人时，可揭去塑料薄膜，铺上麻袋或草帘，用水浇透，有条件时尽量蓄水养护。
3.5截面较大的柱子，宜用湿麻袋围裹喷水养护，或用塑料膜围裹自生养护，也可涂刷养护液。
3.6墻体混凝土浇筑完毕，混凝土达到一定强度（1-3d）后，应及时松动两侧模板，离缝约3-5mm,在墙体顶部架设淋水管，喷淋养护。拆除模板后，应在墙两侧挂麻袋或草帘等覆盖物，避免阳光直照墙面，连续喷水养护，时间符合上述要求。
4.结束语
裂缝是混凝土结构中普遍存在的一种现象。混凝土裂缝进行认真研究、区别对待，采用合理的方法进行处理，并在施工中采取各种有效的预防措施来预防裂缝的出现和发展，保证建筑物和构件安全、稳定地工作。
参考文献
1.王铁梦．建筑物的裂缝控制[M]．上海：科学技术出版社，l987
2.尹平．混凝土裂缝产生原因及预防处理措施[J]．山西建筑，2008，34（10）：159-160．
关键词：混凝土；裂缝成因；防治措施
Abstract: the concrete crack is the engineering field and is difficult to solve common problems, if the construction of concrete cracks often will affect the structure integrity and durability. Combined with practical experience, from the construction component, change of temperature, volume contraction and construction operation, analyzes the concrete crack during the reason and influence factors, put forward the concrete cracks during the control technology, in how to carry on the concrete to crack control of research and practice have some guiding significance.
Keywords: concrete; Crack is presented; Prevention and control measures
中图分类号： TU528 文献标识码：A 文章编号：
引言：下面就混凝土裂缝的成因与控制谈谈。
1.裂缝的成因
裂缝产生的形式和种类很多，要根本解决混凝土中裂缝问题，需要从混凝土裂缝的形成原因入手。正确判断和分析混凝土裂缝的成因是有效地控制和减少混凝土裂缝产生的最有效的途径。
1.1设计原因
1.1.1设计结构中的断面突变而产生的应力集中所产生的构件裂缝。
1.1.2设计中对构件施加预应力不当，造成构件的裂缝(偏心、应力过大等)。
1.1.3设计中构造钢筋配置过少或过粗等引起构件裂缝(如墙板、楼板)。
1.1.4设计中未充分考虑混凝土构件的收缩变形。
1.1.5设计中采用的混凝土等级过高，造成用灰量過大，对收缩不利。
1.2材料原因
1.2.1粗细集料含泥量过大，造成混凝土收缩增大。集料颗粒级配不良或采取不恰当的间断级配，容易造成混凝土收缩的增大，诱导裂缝的产生。
1.2.2骨料粒径越细、针片含量越大，混凝土单方用灰量、用水量增多，收缩量增大。
1.2.3混凝土外加剂、掺和料选择不当、或掺量不当，严重影响混凝土收缩。
1.2.4水泥品种原因，矿渣硅酸盐水泥收缩比普通硅酸盐水泥收缩大、粉煤灰及矾土水泥收缩值较小、快硬水泥收缩大。
1.2.5水泥等级及混凝土强度等级原因：水泥等级越高、细度越细、早强越高对混凝土开裂影响很大。混凝土设计强度等级越高，混凝土脆性越大、越易开裂。
1.3混凝土配合比设计原因
1.3.1设计中水泥等级或品种选用不当。
1.3.2配合比中水灰比(水胶比)过大。2009年，本人负责大江村民公寓工程现场监理工作，该工程在进行二层楼板砼的捣制时，由于混凝土搅拌站提供的混凝土出现水灰比比例调配不当，以致影响到混凝土的凝结期。由于发现及时，立即采取措施加强养护，加上养护妥当，使得该层楼板砼强度达到设计要求，不致造成返工。
1.3.3单方水泥用量越大、用水量越高，表现为水泥浆体积越大、坍落度越大，收缩越大。
1.3.4配合比设计中砂率、水灰比选择不当造成混凝土和易性偏差，导致混凝土离淅、泌水、保水性不良，增加收缩值。
1.3.5配合比设计中混凝土膨胀剂掺量选择不当。
1.4施工及现场养护原因
1.4.1现场浇捣混凝土时，振捣或插入不当，漏振、过振或振捣棒抽撤过快，均会影响混凝土的密实性和均匀性，诱导裂缝的产生。
1.4.2高空浇注混凝土，风速过大、烈日暴晒，混凝土收缩值大。
1.4.3对大体积混凝土工程，缺少两次抹面，易产生表面收缩裂缝。
1.4.4大体积混凝土浇注，对水化计算不准、现场混凝土降温及保温工作不到位，引起混凝土内部温度过高或内外温差过大，混凝土产生温度裂缝。
1.4.5现场养护措施不到位，混凝土早期脱水，引起收缩裂缝。
1.4.6现场模板拆除不当，引起拆模裂缝或拆模过早。
1.4.7现场预应力张拉不当(超张、偏心)，引起混凝土张拉裂缝。
2.裂缝的控制措施
2.1设计中的“抗”与“放”在建筑设计中应处理好构件中“抗”与“放”的关系
所谓‘抗’就是处于约束状态下的结构，没有足够的变形余地时，为防止裂缝所采取的有力措施，而所谓“放”就是结构完全处于自由变形无约束状态下，有足够变形余地时所采取的措施。设计中应尽量避免结构断面突变带来的应力集中。如因结构或造型方面原因等而不得以时，应充分考虑采用加强措施；积极采用补偿收缩混凝土技术：常见的混凝土裂缝中，有相当部分都是由于混凝土收缩而造成的。要解决由于收缩而产生的裂缝，可在混凝土中掺用膨胀剂来补偿混凝土的收缩，实践证明，效果是很好的。
2.2材料选择和混凝土配合比
设计方面根据结构的要求选择合适的混凝土强度等级及水泥品种、等级，尽量避免采用早强高的水泥；选用级配优良的砂、石原材料，含泥量应符合规范要求；积极采用掺合料和混凝土外加剂，可以降低水泥用量、降低水化热、改善混凝土的工作性能和降低混凝土成本的作用；正确掌握好混凝土补偿收缩技术的运用方法。对膨胀剂应充发考虑到不同品种、不同掺量所起到的不同膨胀效果。应通过大量的试验确定膨胀剂的最佳掺量；配合比设计人员应深入施工现场，依据施工现场的浇捣工艺、操作水平、构件截面等情况，合理选择好混凝土的设计坍落度，针对现场的砂、石原材料质量情况及时调整施工配合比，协助现场搞好构件的养护工作 。混凝土是非均质的三相体，即固体、液体和气体。两种相接触的面称为界面，混凝土中界面的存在是无法避免的，对混凝土性能产生不良影响。混凝土拌合物三相所占的体积大致为，固相占总体积的73%~84%、液相占15%~22%、气相占1%~5%。三相体积的改变是混凝土产生裂缝主要原因之一，尤其是混凝土产生终凝之前较为明显（即通常认为随行收缩，干燥收缩等引起的裂缝），但这种裂缝如果在浇筑后及时采取有效的养护措施，能够获得明显的控制效果。
2.2.1混凝土配合比除应按《普通混凝土配合比设计规程》JGJ55的规定，根据要求的强度等级、抗渗等级、耐久性及工作性等进行配合比设计外，其配制的混凝土还应符合4.3.2-4.3.10的规定。
2.2.2干缩率。混凝土90d的干缩率宜小于0.06%。
2.2.3坍落度。在满足施工要求的条件下，尽量采用较小的混凝土坍落度；基础、梁、楼板、屋面用的混凝土坍落度宜小于120mm，柱、墙用的混凝土坍落度宜小于150mm；混凝土采用泵送时，高层建筑用的混凝土坍落度根据泵送高度宜控制在180mm左右，多层及高层建筑底部的混凝土坍落度宜控制在150mm。
2.2.4用水量。不宜大于170kg/m3。
2.2.5水泥用量。普通强度等级的混凝土宜为270-450千克每立方米，高强混凝土不宜大于550千克每立方米。
2.2.6水胶比。应采用较小的水胶比。混凝土水胶比不可大于0.60。
2.2.7砂率。在满足工作性要求的前提下，应采用较小的砂率。
2.2.8宜采用引气剂或引气减水剂。
3.混凝土的养护
3.1养护是防止混凝土产生裂缝的重要措施，必须充分重视，并制定养护方案，派专人养护工作。2004年本人负责世纪嘉园项目的现场监理工作，该项目有1层8000多平方米的地下室，当进行地下室面板施工时，刚好六月初，天气较炎热，刚开始捣制地下室面板时，由于施工方养护措施不当，导致部分面板出现不同程度的裂缝，在发现上述问题后，项目监理部立即组织施工方开会分析原因：由于天气炎热养护不够造成开裂，立即制定落实养护措施，并要求施工方派专人定时负责养护，由于发现及时，加上后期养护措施得当，该地下室面板后期没有再出现裂缝，该例子充分体现混凝土养护的重要性。
3.2混凝土浇注完毕，在混凝土凝结后即须进行妥善的保温、保湿养护，尽量避免急剧变化、振动以及外力的扰动。
3.3浇筑后采用覆盖、晒水、喷雾或用薄膜保湿等养护措施；保温、保湿养护时间，对硅酸盐水泥、普通硅酸盐水泥或矿渣硅酸盐水泥拌制的混凝土，不得少于7d；对掺用缓凝型外加剂或抗渗要求的混凝土，不得少于14d。
3.4底板和楼板等平面结构构件，混凝土浇筑收浆和抹压后，用塑料薄膜覆盖，防止表面水份蒸发，混凝土硬化才可上人时，可揭去塑料薄膜，铺上麻袋或草帘，用水浇透，有条件时尽量蓄水养护。
3.5截面较大的柱子，宜用湿麻袋围裹喷水养护，或用塑料膜围裹自生养护，也可涂刷养护液。
3.6墻体混凝土浇筑完毕，混凝土达到一定强度（1-3d）后，应及时松动两侧模板，离缝约3-5mm,在墙体顶部架设淋水管，喷淋养护。拆除模板后，应在墙两侧挂麻袋或草帘等覆盖物，避免阳光直照墙面，连续喷水养护，时间符合上述要求。
4.结束语
裂缝是混凝土结构中普遍存在的一种现象。混凝土裂缝进行认真研究、区别对待，采用合理的方法进行处理，并在施工中采取各种有效的预防措施来预防裂缝的出现和发展，保证建筑物和构件安全、稳定地工作。