来源 :机械工人 | 被引量 : 0次 | 上传用户:sharongd
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
根部焊道焊接(又称打底焊)质量的好坏是关系到焊缝成功与否很关键的第一步,焊接缺陷往往容易发生在这个地方。在进行管子对接时,因此时无法进行双面焊,但又要要求管子内壁成型光滑、均匀、无裂缝,要想获得高质量的焊缝是比较困难的。本文向您介绍的根部焊道加熔化嵌条的方法,就能很好的解决上述问题。嵌条(顶置填充金属)可用一般氩弧焊方法来熔化,这点尤其有利于管子或封闭型的 Root weld (also known as backing welding) quality is related to the success or failure of the weld is a crucial first step, welding defects are often prone to occur in this place. In the pipe butt, so when can not be double-sided welding, but also require the pipe wall molding smooth, uniform, no cracks, in order to obtain high-quality weld is more difficult. This article introduces you to the root of the weld bead with the method of melting can be a good solution to the above problems. The fillet (top-fill metal) can be melted by a common argon arc welding method, which is especially advantageous for pipes or closed-type
其他文献
感应淬火的轴类零件非常适用于大多数扭转场合。这是因为感应淬火增加了表面附近所最需要的硬度,并且在表面产生了改善疲劳寿命的压应力。当一根轴承受扭转载荷时,表面的剪
在腐蚀性介质中,加入少量的一种或数种物质,能使金属的腐蚀速度大大降低,这种物质或复合物就称为缓蚀剂。缓蚀剂作为一门防蚀技术,这些年来得到了迅速的发展,被保护金属由单
GCr15钢丝的生产过程必须以球化退火做预处理,同时中间退火次数多,生产周期长,金属损耗大,影响经济效益,因而查清其拉拔性能,以制定经济合理的拉拔工艺是非常必要的。在一定
我们加工偏心工件(图1)时,采用了装夹方便的夹具(图2)。工件首先按偏心要求粗车留余量,再车削图中未注偏心的各直径尺寸至图纸要求。在制作夹具时,轴套2粗车后攻好丝孔,再装
《蒸汽锅炉安全监察规程》要求“锅筒的全部对接焊缝和集箱的纵向对接焊缝应进行100%射线探伤或者100%超声波探伤加至少25%射线探伤”。在编制焊缝X射线探伤工艺时注意到,对焊
因工作需要,本刊现面向全国招聘美术编辑一名,要求熟悉和热爱足球,具有较高的平面媒体设计水平,富于创新意识,敢于接受挑战,并且适应加班工作的需要,不论你是具有相关工作经
本文叙述了滴流除气和钢包除气的历史发展,阐明了真空冶金和有关反应的理论,并比较了现有各类真空除气装置。本文还论述了真空处理的程度,而且参照工作结果进一步确认了用不
树突棘是兴奋性突触的主要突触后结构基础,其数量与形态受神经电活动调控,并在整个生命过程中呈现复杂且有序的动态变化。树突棘的动态变化在神经环路的形成和精确化修剪中扮
从2008年到2009年,从时间的角度而言只是又过去了一年,但换个视角,会发现就中国体育而言,无疑跨过了一个新的时代,中国体育让我们感受到了全面成长的力量。在贝尔格莱德举行
思维是理性认识及其过程。科学思维是以辩证思维为核心的思维,既包括世界观和方法论,又包括科学理论和科究方法。科学思维是人类意识活动的高级形式,是客观事物和现象在人的