制备了两种磁性材料与聚苯胺合成的材料，采用３ｃｍ波导式测量线在８ＨＧｚ－１４ＧＨｚ频率范围内，测量有关数据，用多点拟合的实验方法和计算方法对这类复合聚苯胺的电磁参数及微波吸收特性曲线参数进行了测量．实验结果表明，通过调节磁性材料与苯胺的反应质量比例，从而可以调节复合聚苯胺的电导率，进而调节其电磁参数，最终可以达到调节反射系数Ｒ，并找到最大Ｒ值及最大吸收频宽的目的．
Two kinds of materials synthesized with polyaniline were prepared. The measurement data of the 3cm waveguide was measured in the frequency range of 8HGz-14GHz. The data were measured. The experimental data of the polyaniline Parameters and microwave absorption curve parameters were measured. Experimental results show that by adjusting the reaction mass ratio of the magnetic material and the aniline, the conductivity of the composite polyaniline can be adjusted and the electromagnetic parameters can be adjusted. Finally, the reflection coefficient R can be adjusted and the maximum R value and the maximum absorption bandwidth can be found purpose.