对结构钢用末端淬火法测定其淬透性时,按GB225—63的规定进行。在最后测量其硬度HRC时,规定指出:“试样应在夹具中沿两磨制平面的中心线进行硬度测量”,“测量硬度系由试样末端起每隔1.5毫米测量一次”。但在规定中对所用夹具没有明确的规定与说明。不少单位为满足规定要求,就先在试样上划好线,然后再测定硬度。显然这样不仅操作麻烦而且准确性亦差。为此我们考虑了如下图所示
Structural steel quenching method by the end of determination of its hardenability, according to the provisions of GB225-63. At the end of the measurement of its hardness HRC, the regulation states: “The test specimen shall be measured for hardness in the fixture along the centerline of both grinding planes” and “the measured hardness shall be measured every 1.5 mm from the end of the specimen”. However, the provisions of the fixture used there is no clear rules and instructions. Many units to meet the requirements of the first line on the sample plan, and then determine the hardness. This is obviously not only troublesome operation but also accuracy is poor. For this reason we consider the following figure