This is a synthetical report about hydrogen behavior in titanium aluminide alloys in our group. There are two kinds of hydrogen solubility in titanium aluminides, one is the overall solubility at high temperature in the matrix without hydride and the other is the terminal solubility at low temperature in the matrix in equilibrium with the hydride. The former decreases but the later increases with increasing temperature. Hydrogen as a temporary β stabilizer clearly decreases the size of the α2 phase, and increases greatly the amount of β phase, and then increases evidently the mechanical properties of Ti3Al+Nb. The cathodic corrosion of TiAl during charging is due to hydride on the surface. The decrease of the strength, the strain to fracture and fracture toughness for hydrogenated samples is due to hydride. The enrichment of atomic hydrogen at the crack tip during charging under sustained load can enhance localized plastic deformation and cause hydrogen-induced delayed cracking.