【摘 要】
：
Fluoride nanoparticles with multiform crystal structures and morphologies were successfully synthesized by a facile, effective, and environmentally friendly coprecipitation method. Transmission electron microscopy (TEM) was used to characterize the nanopa
【机 构】
：
College of Chemical & Environment Science, Shaanxi Key Laboratory of Catalysis, Shaanxi University o
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
Fluoride nanoparticles with multiform crystal structures and morphologies were successfully synthesized by a facile, effective, and environmentally friendly coprecipitation method. Transmission electron microscopy (TEM) was used to characterize the nanoparticles. The nanoparticles were modified by PEI, CTAB, PAA and Ci, respectively. It was feasible for function by -COOH and -NH2 groups, due to the surface modification. Moreover, different surface modifications of the nanoparticles were examined. The possible formation mechanisms for fluoride nanoparticles with surface modification were presented in detail. More importantly, it is expected to be widely applied to biomedicine.
其他文献
Phase pure ZrB2-SiC composite powders were prepared after 1 450 ℃/3 h via carbothermal reduction route,by using ZrSiO4,B2O3 and carbon as the raw materials.The influences of firing temperature as well as the type and amount of additive on the phase compos
The Lap-joint configuration and the vacuum assisted forming method were put forward to meet the demands of the compression bending strength and the strong connection between the steel and FRC.The bending mechanic tests of the Lap-joint bending specimens c
To obtain the influence laws of the fine gangue rate on the properties of coal gangue cementitious paste, the slump, divergence, stratification, bleeding, setting time and mechanical strength with the change of fine gangue rate were studied on the basis o
The aim of this work was to investigate the effect of waste paper fiber on the properties of cement-based mortar and the relative mechanism. The cement-based mortars with various contents and mixing way of waste paper fibers were prepared and the slump fl
By using redispersible polymer powder (RPP) and carbon fiber (CF) to adjust the flexibility and electrical properties of the smart aggregate, a new kind of smart aggregate with Z type structure was proposed. The study shows that Z type aggregate is more s
An attractive way to prepare W/TaC based cermet at a relatively low temperature was proposed and confirmed experimentally. The thermodynamics calculations indicated that the reaction between WC and Ta2O5 was feasible at as low a temperature as 1400 ℃. The
The influence of air-cooled blast furnace slag aggregates as replacement of natural aggregates on the water absorption of concrete and mortar was studied, and the mechanism was analyzed. The interface be-tween aggregate and matrix in concrete was analyzed
The stress–strain behavior and strain rate sensitivity of pre-strained Ni80Cr20 (Ni20Cr) were studied at strain rates from 4.8×10–4 s–1 to 1.1×10–1 s–1. Specimens were prepared through cold drawing with abnormal plastic deformation. The texture of the spe
We have developed a controlled-release drug carrier. Smartly controlled-release polymer nanoparticles were firstly synthesized through RAFT polymerization as the controlled-release core. The structural and particle properties of polymer nanoparticles were
Alloy powders including Ni60, WC, Cr3C2, and TiC with different mass ratios were deposited on medium carbon low alloy steel by plasma welding. Through the experiments, the optimal alloy powder rein-forcing cutter tool surface properties were discovered. T