The aim of this work is to attempt the application of A357 Al-Si-Mg cast alloy in the thixoextrusion process,evaluating the different forming parameters effect.Thixoextrusion offers several advantages compared with traditional hot-extrusion such as lower pressure,minor friction forces,higher material fluidity and longer tool life.This type of semi-solid process requires high solid fraction(0.70.85) is less sensitive to temperature drops and allows more stable material flow at higher speeds.To know the forming parameters that improve the mechanical properties of thixoextruded parts,some extrusion tests were carried out.The results were used as the main criteria for assessing the thixoforming viability of the A357 alloy.
The aim of this work is to attempt the application of A357 Al-Si-Mg cast alloy in the thixoextrusion process, evaluating the different forming parameters effect. Hixoextrusion offers several advantages compared with traditional hot-extrusion such as lower pressure, minor friction forces, higher material fluidity and longer tool life. This type of semi-solid process requires high solid fraction (0.7 0.85) is less sensitive to temperature drops and allows more stable material flow at higher speed. To know the formin g parameters that improve the mechanical properties of thixoextruded parts, some extrusion tests were carried out. the results were used as the main criteria for assessing the thixoforming viability of the A357 alloy.