奥-贝球铁中贝氏体形态的电镜观察

来源 :浙江大学学报(自然科学版) | 被引量 : 0次 | 上传用户:lpucicy
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
奥-贝球墨铸铁具有良好的综合性能。作者采用低速切割、机械磨抛和最终的低角度离子减薄的方法成功地制备了供透射电镜观察用的球铁薄膜,电子衍射和相应的衍射像表明,球铁经900℃奥氏体化一小时,并于370—380℃盐浴中等温一小时三十分后,其形态为板条状贝氏体铁素体,其间有奥氏体,未发现渗碳体存在,经X射线衍射测定残留奥氏体量为30%。 Austria - Bay ductile iron has a good overall performance. The author successfully prepared the ductile iron film for transmission electron microscopy by low speed cutting, mechanical grinding and final low angle ion reduction. The electron diffraction and the corresponding diffraction images show that the ductile iron is austenitized at 900 ℃ One hour, and in the 370-380 ℃ salt bath for an hour and a half after the temperature, the form of lath bainitic ferrite, with austenite in between, did not find the presence of cementite, X-ray diffraction The amount of retained austenite was determined to be 30%.
其他文献
采用带材厚0.2mm、冲压成形高度(HO)为0.33mm的碟形弹簧,如何进行行程(F)及力(N)的测量,该碟形弹簧的行程只有0.075mm,外界各种因素对行程和力的影响比较大。因此采用一般测
此装置的主要构造如图1所示,由五个部件构成:1是用来作为光标尺的普通40w日光灯管,外包一层刻有厘米标度的照相胶卷黑衬纸,用来量度位移。2是用来承接“落体”的缓冲网袋。3
汕府[2015]10号市政府各部门、各直属机构:现将《广东省人民政府关于发布〈广东省政府核准的投资项目目录(2014年本)〉的通知》(粤府[2015]3号)转发给你们,请认真按照执行。2
在检验工作中,我们常常遇到一些大型结构件不易上平台测量(因为工件大于检测平台),而在地面上检查,则不好找基准。但是这些大型构件往往都有一定技术要求。针对这种情况,我
新课标《地理》七年级上册(人教版)第一章《地球和地图》、第二章《陆地和海洋》1.游戏探究——用经纬网确定位置,探究规律。活动目的:让学生知道地球上任何一点的位置均可
模拟闭塞腐蚀电池的发生过程,研究了OCr 18Ni 9Ti奥氏体不锈钢在pH=6.86的3% NaCl溶液中,在承受一定拉应力的情况下,闭区内试样段电位和介质pH值随闭区外试样段极化电位变化的
本研究曾经试验性地测定了两种含硅贝氏体钢的断裂韧性,并阐明了断裂韧性和钢的显微结构的关系。具有高强度和高韧性相结合的最佳贝氏体显微组织由贝氏体铁素体和取代渗碳体
一、锻模硬度与寿命的关系锤上锻模合适的热处理硬度应该保证它在热工作状态下具有最佳的综合机械性能——足够的强度、耐磨性和冲击韧性,这是防止锻模过早失效的重要条件。
根据化学热力学和动力学、材料的界面科学、内扩散理论设计出的优质、高速、节能气体渗氮新工艺,经正交试验优选出几种工艺设计,用于实际生产仅20小时就突破了0.50mm的渗层,
本资科是1978年由伊藤忠商事株式会社向中国金属学会提供的。资料共分二个部分。第一部分为钨丝制造过程的简述。第二部分为钨丝的加工设备。现将全文翻译出来供我国钨钼材料