【摘 要】
：
A low-density single crystal (LDS) alloy with the composition of high Mo content was designed.The extra 1.5 wt％ Mo was added in the Alloy A with the composition
【机 构】
：
School of Materials Science and Engineering, Beihang University, Beijing 100191, China
论文部分内容阅读
A low-density single crystal (LDS) alloy with the composition of high Mo content was designed.The extra 1.5 wt％ Mo was added in the Alloy A with the composition of Ni-6.5Al-8.0Mo-2.4Cr-6.2Ta-4.9Co-1.5Re-(0.01-0.05)Y (wt％) to study the influence of Mo on the lattice parameter and partitioning behavior.Scanning electron microscope (SEM) with energy-dispersive spectrometer (EDS),transmission electron microscopy (TEM) and high-temperature X-ray diffraction (HT-XRD) were used to observe the microstructure,analyze the elemental content and measure the lattice parameter of the alloys.The natural lattice misfit was calculated by lattice constants which were measured by HT-XRD at the temperature from 25 to 1150 ℃,and the results showed that the lattice misfit would be more and more negative with temperature increasing.It was found that 1.5 wt％ addition of Mo will increase the absolute value of the lattice misfit of γ/γ′phases and the volume fraction of γ′,and at the same time,influence the elemental distribution in γ and γ′ phases,especially Re and Cr.Re has a higher partitioning ratio (k) after the addition of Mo.
其他文献
A comparative study based on MgH2 ball-milled with altered Ni particle sizes under different conditions was conducted to reveal the effect of close contact betw
Hydrogen nuclear magnetic resonance (H1-NMR) and X-ray diffractometer (XRD) were used to characterize the molecular and crystal structure of lead methacrylate[P
Here,carbon dots (CDs) only or nanocomposites of CDs and TiO2 (CDs-TiO2) were used to decorate titanium dioxide nanotube arrays (TiO2NTs) in situ by solvotherma
在淤泥层中,顶管顶进施工过程对上覆土体和邻近管线的影响较大,合理调节相关施工参数对控制土体扰动具有重要意义.本文以深圳固戍污水净化厂二期工程配水管项目为例,通过有限
γ'+ β Binary-phase Ni-Al coatings were prepared on second-generation single-crystal superalloy René N5 (N5) substrates by electron beam physical vapor deposi
NiCoCrAlY is usually used as the material to bond-coat in thermal barrier coating systems under high temperatures.Using NiCoCrAlY and adding different amounts o
心理学研究表明,当学习内容与学生的生活背景越接近,学生自觉接纳的程度就越高,越有兴趣。而小学生已经具备了一定的生活经验,同时他们对周围的各种事物、现象又充满着好奇,
《建议》提出了“十二五”时期我国经济社会发展主要目标,对于科学制定“十二五”规划,继续抓住和用好我国发展的重要战略机遇期、促进经济长期平稳较快发展和经济发展方式转
为了固化某磷矿分解车间产生的含铅镉离子工业固废中的重金属离子,本文以该工业固废为研究对象,通过室内试验从6种固化剂中选定最优固化剂,研究在不同掺量、试样含水率和粒径
There is an urgent demand to explore new approaches of improving the electric breakdown strength of the ferroelectric thin-film capacitor without the degradatio