论文部分内容阅读
A survey of solder ball production processes especially focusing on disturbed molten metal jet breakup process was made. Then the formation of capillary wave on tin melt jet in the way of rapid solidification was studied. A semi-empirical formula, which can be written as λ = Cvib (σ/ρ)1/3f-2/3 to predict the relationship between wavelength of capillary wave and frequency of imposed vibration was obtained. Sn-4.0Ag-0.5Cu lead free solder ball was successfully produced with tight distribution and good sphericity. The excited jet breakup process is promising for cost effectively producing solder ball.