【摘 要】
：
The effects of substituting Co for Fe on the microstructure and stress rupture properties of K4750 alloy were studied.The microstructure of the alloy without Co (K4750 alloy) and the alloy containing Co (K4750-Co alloy) were analyzed.Substitution of Co fo
【机 构】
：
Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China;School of Materials
论文部分内容阅读
The effects of substituting Co for Fe on the microstructure and stress rupture properties of K4750 alloy were studied.The microstructure of the alloy without Co (K4750 alloy) and the alloy containing Co (K4750-Co alloy) were analyzed.Substitution of Co for Fe inhibited the decomposition of MC carbide and the precipitation of η phase during long-term aging treatment.In K4750-Co alloy,the morphology of MC carbide at the grain boundary (GB) remained dispersed blocky shape and no η phase was observed after aging at 750 ℃ for 3000 h.However,in K4750 alloy,almost all the MC carbides at GBs broke down into granular M23C6 carbide and needle-like η phase.The addition of cobalt could delay the decomposition of MC carbides,which accordingly restricted the elemental supply for the formation of η phase.The stress rupture tests were conducted on two alloys at 750 ℃/430 MPa.When Co is substituted for Fe in K4750 alloy,the stress rupture life increased from 164.10 to 264.67 h after standard heat treatment.This was mainly attributed to increased concentration of Al,Ti and Nb in γ\'phase in K4750-Co alloy,which further enhanced the strengthening effect of γ\'phase.After aging at 750 ℃ for 3000 h,substitution of Co for Fe can also cause the stress rupture life at 750 ℃/430 MPa to increase from 48.72 to 208.18 h.The reason was mainly because MC carbide degradation and η phase precipitation in K4750 alloy,which promoted the initiation and propagation of micro-crack during stress rupture testing.
其他文献
In this work, a series of biodegradable pure iron, Fe-30Mn and Fe-30Mn-Ag alloys were developed by using a rapid solidification technology. A fine α-Fe dendrite was formed in pure iron, resulting in a high compressive yield strength of above 300 MPa. The
In this study, Al-Zn and Al-Mg coatings were deposited on steel substrates by an arc thermal spray process. X-ray diffraction and scanning electron microscopy were used to characterize the deposited coatings and corrosion products. Open circuit potential
Porous TiAl3 intermetallics were fabricated through vacuum reactive sintering from Ti-75Al at.％ elemental powder mixture.The phase compositions,expansion behaviors,pore characteristics and microstructure evolution of TiAl3 intermetallics were investigated
Perovskite material is one of the promising classes of redox catalysts for hydrogen production through two-step thermochemical H2O splitting.Herein,an analogue of La1-xCaxMnO3 perovskite was systematically investigated as a catalyst for thermochemical H2
To refrain the interdiffusion of elements while holding good oxidation resistance,a (Ni,Pt)A1/Ni composite coating was prepared by sequential treatments of electroplating Ni and Pt and successive gaseous aluminization.In comparison with normal (Ni,Pt)Al c
Atom probe tomography was utilized to investigate Cu precipitation in a high-strength low-alloy steel isothermally aged at 500 ℃ for 1,4,16,and 64 h after water-quenching from 900 ℃.With prolonged aging time,the Curich precipitates (CRPs) increased in siz
In this work, the serpentine powders were sintered to make the serpentine-reinforced Al-matrix composites, and the microstructures of which were characterized by differential scanning calorimetry, thermal gravimetric analyzer, and X-ray diffractometer. Sc
The Stern-Geary constant (B value) is indispensable to measure the corrosion rate in the microbiologically influenced corrosion (MIC) systems.Linear polarization resistance (LPR) and weight loss methods were used to study the variation of B values for X80
The effect of γ-phase on two-way shape memory effect (TWSME) of polycrystalline Ni56Mn25-xCoxGals.9Gd0.1 alloys was investigated.The results show that an appropriate amount of ductile γ-phase significantly enhances the TWSME.The largest TWSME of 1.4％ with