Tin bronze wires were produced by dieless drawing. The effects of heating power, the distance between cooler and heater as well as feeding speed on the diameter, the temperature field, and the deformation region profile of the wires were investigated. The results indi-cated that each processing parameter exhibited both lower and upper limits of stable deformation based on the criterion of stable deformation with the diameter fluctuation of ±0.05 mm. Both the temperature and its gradient of the deformation region increased with increasing heating power under stable deformation, but decreased with an increase in feeding speed. As the distance between cooler and heater increased, the temperature of the deformation region increased and the slope of the deformation region profile decreased. The processing limit map of sta-ble deformation exhibited a closed curve and the unstable deformation consisted of wire breakage and diameter fluctuations. Tin bronze wires were produced by dieless drawing. The effects of heating power, the distance between cooler and heater as well as feeding speed on the diameter, the temperature field, and the deformation region profile of the wires were investigated. that each processing parameter exhibit both both lower and upper limits of stable deformation based on the criterion of stable deformation with the diameter fluctuation of ± 0.05 mm. Both the temperature and its gradient of the deformation region increased with increasing heating power under stable deformation, but but with an increase in feeding speed. The process of limiting deformation of the deformation region increased and the slope of the deformation region profile decreased. consisted of wire breakage and diameter fluctuations.