SRBI4TI4O15相关论文
利用固相烧结工艺制备了SrBi4Ti4O15(SBTi)铁电陶瓷,研究了过量Bi2O3时SBTi陶瓷烧结特性的影响,结果表明:1)在1150℃以下烧结的Bi......
研究了La掺杂对SrBi4Ti4O1s铁电介电性能影响.当La含量为0.75时得到剩余极化2Pr极大值为17.8 μC/cm2,同时介电常数呈现极大.随La......
期刊
用传统的固相烧结工艺,制备了钼掺杂铁电陶瓷样品SrBi4Ti4O15(SBTi)铁电陶瓷SrBi4-2x/3Ti4-xMoxO15(x=0.00,0.003,0.012,0.03,0.06......
期刊
采用固相烧结工艺制备了SrBi4Ti4O15(SBTi)/Ag铁电复合材料,通过X射线衍射、光学金相显微镜和扫描电子显微镜对材料的组成和微观结......
Synthesis and Microstructure of Partly-oriented Bismuth Layer Structure Ferroelectrics Ceramics SrBi
SrBi4Ti4O15 powder was synthesized by conventional solid state synthesis (CS) and molten salt synthesis (MSS). MSS metho......
采用传统固相烧结工艺,制备了掺杂量分别为0.00～1.00、0.00～0.06的La、V掺杂SrBi4Ti4O15铁电陶瓷.X射线衍射结果显示,La、V对SrBi4Ti......
采用熔盐法制备了各向异性生长的SrBi4Ti4O15粉体，研究了工艺参数对晶粒形貌和尺寸的影响。发现煅烧温度、盐的种类和盐的用量显著......
利用固相烧结工艺制备了SrBi4Ti4O15（SBTi）铁电陶瓷，研究了过量Bi2O3对SBTi陶瓷烧结特性的影响，结果表明：在1150℃以下烧结的Bi不过量的......
The structure and properties of Mg-doped SrBi4Ti4O15(SBT) were dicussed. Mg substitution into SBT had two possibilities ......
用高温固相烧结法制备了SrBi4Ti4O15（SBTi）铁电陶瓷，用双氧水浸泡72h进行氧处理的样品与未经过氧处理的样品进行对比研究。样品的介电......
研究了La掺杂对SrBi4Ti4O13铁电介电性能影响，当La含量为0.75时得到剩余极化2Pr极大值为17.8μC/cm^2，同时介电常数呈现极大。随La掺......
采用同相法和熔盐法（KCl-NaCl作为熔盐）合成SrBi4Ti4O15陶瓷粉体，用模板晶粒定向技术（TGG）获得具有各向异性晶粒定向排列的SrBi4Ti4O15......
通过对La不同掺杂比例SBT的XRD、拉曼光谱测试表明La掺杂对铋层状结构材料SBT的结构没有破坏。随掺杂量增加La取代不同位置，SBT拉曼......
采用NaCl-KCl熔盐法合成了生长各向异性的片状SrBi4Ti4O15粉体，用XRD分析了粉体相的结构，用SEM观察了粉体的微观形貌，讨论了不同预烧......
采用传统固相反应法制备了Sr1–xBaxBi4Ti4O15（x=0～1.0）铁电陶瓷,研究了Ba取代量对其烧结性能和介电性能的影响。结果表明,适量Ba取代......
期刊