Strongly segregated polyethylene-b-polystyrene (PE-b-PS) diblock copolymers were infiltrated within anodic aluminum oxide nanoporous templates (AAO) (with 60 nm diameter).After carefully removing the
【机 构】
:
POLYMAT and Polymer Science and Technology Department,Faculty of Chemistry,University of the Basque
【出 处】
:
Seventh International Symposium On Engineering Plastics (第七届
论文部分内容阅读
Strongly segregated polyethylene-b-polystyrene (PE-b-PS) diblock copolymers were infiltrated within anodic aluminum oxide nanoporous templates (AAO) (with 60 nm diameter).After carefully removing the nanofibers from the nanopores, TEM revealed their morphology.This is the first time that the morphology of semi-crystalline diblock copolymers infiltrated within AAO templates is observed.Regardless of their composition and initial phase segregated morphology (i.e., lamellae,cylinders or spheres), the infiltrated nanofibers are constituted by core-shell (see Figure 1) or pseudo core shell self-assembled nanocylinders.
其他文献
Thermoplastic elastomers (TPEs) are generally entropic networks with micro-phase separated morphology.They are made of flexible chain segments which impart elastic properties and physical crosslinks w
Biodegradable polymers have shown great potentials in biomedical field and environment protection.As an inherant property, biodegradability has been widely investigated in terms of weight loss, morpho
Polymer solar cells (PSCs) have attracted considerable interests in making larger-area devices through roll-to-toll printing process for its advantage of low-cost and rich raw materials.Bulk heterojun
Carbon composites using polymer resins as binder and carbon black or mesophase pitch as additives were investigated aiming to develop optimum compositions with advanced performance in manufacture new
Dental caries and dental erosion are two major problems of oral health.In comparison to dental caries, which have been well controlled by fluoride, dental erosion, tooth mineral loss due to the acid,
Time-of-flight secondary ion mass spectrometry (ToF-SIMS) spectra of polystyrene (PS)1 and poly (2,3, 4, 5, 6-pentafluorostyrene) (5FPS)2 films supported on silicon wafers were obtained at temperature
Nature has used brush like soft matters and hydration lubrication to achieve ultra-low friction even at high Herzian pressure, such as in articular cartilage.Inspired by this, people have used polymer
In this work, we present rheological study on the linear and nonlinear viscoelasticity of polymer/silica nanocomposites.It is well known that network of particle agglomerates can form when the content
Since free ends play an important role in the motion of entangled polymers (reptation, fluctuations),examining the behaviour of ring polymers (which have no beginning or end) is a challenge.In fact,th
Supramolecular polymer networks are formed by non-covalent associative interactions between polymer chains.The reversibility of the crosslinks leads to a wide range of potential applications of these