Synthesis of 3Mg(OH)2·MgCl2·8H2O nanowires from agglomerated Mg(OH)2 microspheres

来源 :The 6th International Conference on Hydrometallurgy(第六届国际湿法冶 | 被引量 : 0次 | 上传用户:ysd007
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
A calcination-hydration-conversion method was developed to synthesize magnesium hydroxide chloride hydrate (3Mg(OH)2·MgCl2·8H2O, MHCH) nanowires from agglomerated Mg(OH)2 microspheres,focusing mainly on the influence of the activities of Mg(OH)2 precursors on the morphology of MHCH nanowires.
其他文献
Selective acid Leach and beneficiation process was carried out to recover gallium from slag containing gallium.The experiment results of acid leaching tests showed that the leaching rate of Ga, A1 and
At present, lithium air battery has attracted a great deal of attention because of its higher theoretical energy density than all other battery types.In a lithium air battery, catalysts, such as trans
会议
The neodymium oxalate and neodymium oxide with large particle size was prepared in present study.Precipitate formation of neodymiumn oxalate was obtained in P507-N235-kerosene-cyclohexane system.
会议
Selective acid Leaching and beneficiation process was carried out to recover gallium from gallium-containing slag.The experiment results of acid leaching tests showed that the leaching rate of Ga, A1
Agglomeration is a process that a number of particles adhere together to form an agglomerate, and is generally divided into two or three steps: encounter and association between particles, consolidati
In this paper, A1 rod lead alloy/β-PbO2 composite anode was prepared on aluminum rod lead alloy by drawing-extrusion composite β-PbO2 particals.After 36h galvanostatic polarization at the current dens
In order to search for a good corrosion resistance, highly electrocatalytic activity and the long service life anode material used in copper electrowinning, Pb-0.06%Ca-1.2%Sn alloy anode was prepared
Flake silver powders with low apparent density of 0.4-0.8g/cm3, high diameter-to-thickness ratio (>125) and particle size of 5-10μ.m were prepared by adjusting the ball grinding process with chemical-
The effects of additives on the zinc electrodeposition were investigated in sulfuric acid solution containing Mg2+ through the characterizations of current efficiency (CE), power consumption (PC), dep
Transition metal oxides (Co3O)4, CoO, NiO, MnO, et al.) are accounted as potential anode materials for high performance Li-ion batteries (LIBs).And the traditional thermal treatment method is usually
会议