Improvement of the CNT Twisted Yarn Using Cardo Epoxy Resin

来源 :The 11th China-Japan joint conference on Composite Materials | 被引量 : 0次 | 上传用户:caway1
下载到本地 , 更方便阅读
声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架
论文部分内容阅读
  CNT yarn is made from CNT bundles.But it is so low in tensile strength for the weak Van der Waals force of CNT each other.Therefore we aimed at the strength improvement of CNT yarn by impregnation of the Cardo structure epoxy resin (CP) that the affinity was good for CNT.In addition,we compared the effect of the strength improvement of the CP with the bis-phenol A epoxy (EP) to CNT yarn
其他文献
The aim of this study is to increase the friction coefficient between.C/C composites at low temperature to moderate the dependence of the frictional coefficient on the temperature condition.
Carbon fiber sandwich structures,with higher specific stiffness,specific strength,energy-absorbed ability,fatigue resistance and thermal functions,have been widely used in aerospace,automotive,marine
该论文综述了负热膨胀系数(NTE)材料和负膨胀纤维强化复合材料。论述了高强UHMW-PE纤维Dyneema和PBO纤维Zylon的细微结构、分子结晶取向及刚性直线分子链的桥原子横向热振动,及由此引起的纤维负膨胀机理。讨论了负膨胀纤维强化复合材料的性能和制备。最后介绍了负膨胀纤维强化复合材料在超导线轴上的应用。
采用光还原法制备出SrTiO3-石墨烯复合光催化剂.利用XRD,FTIR,TEM和紫外-可见漫反射光谱对样品进行了表征.结果表明:SrTiO3纳米颗粒均匀地附着在石墨烯表面,复合样品的带隙约为3.35 eV.
纤维增强陶瓷基复合材料在拉伸载荷作用下,其应力-应变曲线会出现明显的非线性行为,基体开裂、纤维/基体界面脱粘和纤维断裂等损伤机制是其出现非线性的主要原因.采用细观力学方法建立了预测纤维增强陶瓷基复合材料拉伸应力-应变曲线的模型.采用剪滞模型描述复合材料出现损伤后的细观应力场,通过损伤模型确定拉伸载荷下细观损伤参量的演化,将剪滞模型与损伤模型相结合,预测了纤维增强陶瓷基复合材料单轴拉伸应力-应变曲线
聚合物基软磁性复合材料以其耐热性能好、耐腐蚀、韧性好、易加工和相对密度低等优点而被广泛应用于电子技术、通讯、汽车、航天航空等诸多领域。本文采用环氧树脂WSR-615和AG-80为基体,以Fe-Si磁性颗粒为填料,通过热压成型方法制备了高含量软磁性树脂基复合材料,并对复合材料的热性能、力学性能和磁性能进行了研究。
In-situ generated MgAl2O4 nanowhiskers reinforced 6061 aluminum (Al) alloy composites have been successfudly synthesized by reaction hot pressing under a relatively low temperature (600 ℃).
通过建立复合材料单向加筋壁板单元的基本力学假设和计算分析模型,提出了一种综合分析其结构力学性能和多约束条件下进行快速优化分析的方法,并利用该方法对典型的复合材料单向加筋壁板结构进行了结构效率分析和优化,得到了其结构效率随各设计参数的变化趋势和相对最优结构参数,为复合材料单向加筋板的设计提供直接参考。本文方法综合考虑筋条总体稳定性、局部稳定性、结构静强度约束及其之间相互影响,并在基本假设的基础上将复
Ultrasonic welds between crystalline and anmorphous polymers of PMMA-PLA and PMMA-POM are carried out,especially for the immiscible materials pair of PMMA-POM.Both of the effects of welding conditions
In the context of developing multi-functional composites [1],our efforts have been devoted in exploring ideal functional fillers that could meet the criteria: (i) a likely omnipotent functional filler