The recrystallization kinetics at 530℃ of twin roll casting Al-Mn alloys with and without low temperature pre-recovery was investigated.It was revealed that the samples with/without pre-recovery exhibited differences in recrystallization kinetics, despite the fact that concurrent precipitations were generated in both cases.